通过薄板坯连铸连轧(TSCR)生产典型低碳铝镇静钢SPHC(一般用热轧钢带)流程的实验室模拟,分析了含(10-50)×10-6B,0.005%N热轧钢带的组织、析出物的特点以及性能变化结果表明:由于粗大BN的优先析出抑制了细小AlN的析出,提高了晶粒的生长能力,以及B在奥氏体晶界的偏聚抑制了铁素体形核,使得含B热轧钢带晶粒明显粗化,通过测定,含B钢晶粒度达到7-8级,平均晶粒尺寸达到25 μm.含B钢晶粒粗化以及钢中AlN析出量和自由N含量的降低,使得热轧钢带屈服强度与无B钢相比降低约94 MPa.
参考文献
| [1] | Takahashi N,Shibata M.Conf Proc on Technology of Continuous Annealed Cold-Rolled Sheet Steel,Warrendale,PA:TMS-AIME,1984:133 |
| [2] | Sudo M,Tsukatani I.Conf Proc on Technology of Continuous Annealed Cold-Rolled Sheet Steel.Warrendale,PA:TMS-AIME,1984:203 |
| [3] | Kang Y L,Yu H.Sci Technol Eng,2005; 5(5):305(康永林,于浩.科学技术与工程,2005;5(5):305) |
| [4] | Gao N,Baker T N.ISIJ Int,1998; 38; 7:744 |
| [5] | Manohar P A.ISIJ Int,1998; 38:799 |
| [6] | Miyahara M,Nakajima N,Kuramoto K.R&D Kobe Steel Enpinering Rep,1990; 36(3):61(宫原征行,中岛悟博,藏本腾次郎,R.D神户制钢技报,1990;36(3):61) |
| [7] | Choquet P,Febregue P,Giusti J,Chamont B,Pezant J N.Int Symup on Mathematical Modeling of Hot Rolling of Steel,Canada,1990; 33 |
| [8] | Yong Q L,Sun X J,Liu Q Y,Zhang C,Li J K.Spec Steel,2005; 26(1):1(雍岐龙,孙新军,刘清友,张晨,李继康.特殊钢,2005;26(1):1) |
| [9] | Cahn R W,Haasen P,Kramer E J.Translated by Liu J H et al.Materials Science and Technology.Vol.7,Beijing:Science Press,1999:97(Cahn R W,Haasen P,Kramer E J.刘嘉禾等译.材料科学与技术丛书.第7卷,北京:科学出版社,1999:97) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%