以Ti-43Al-3Si为籽晶,研究了不同抽拉速率对TiAl合金籽晶法定向凝固全片层组织的影响.结果表明,60 mm/h抽拉速率下,凝固组织中的片层方向能够与生长方向保持一致.随抽拉速率增加,由于温度梯度降低、成分过冷增大等因素的影响,凝固组织中出现了与生长方向成45°或90°夹角的片层取向.电磁搅拌引起的强制对流使固/液界面前沿的扰动不断增强,晶体生长形态发生变化,破坏了片层取向的一致性.
参考文献
| [1] | Inui H,Kishida K,Misaki M,Kobayashi M,Shirai Y,Yamaguchi M.Philos Mag,1995; 72A:1609 |
| [2] | Kim S E,Lee Y T,Oh M H,Inui H,Yamaguchi M.Mater Sci Eng,2002; A329-331:25 |
| [3] | Kim S E,Lee Y T,Oh M H,Inui H,Yamaguchi M.Intermetallics,2000; 8:399 |
| [4] | Chen G L,Lin J P.Ordered Intermetallics Structural Material.Beijing:Metallurgical Industry Press,1998:736(陈国梁,林均品.有序金属间化合物结构材料.北京:冶金工业出版社,1998:736) |
| [5] | Yamaguchi M,Inui H.Structural Intermetallics.Warrendale:TMS,1993:127 |
| [6] | Kim Y W.JOM,1994; 46:30 |
| [7] | Zheng X Q,Shen J,Ding H S,Chen R R,Xu X.Mater Rev,2005; 19(3):118(郑循强,沈军,丁宏升,陈瑞润,许雄.材料导报,2005;19(3):118) |
| [8] | Yamaguchi M,Johnson D R,Lee H N,Inui H.Intermetallics,2000; 8:511 |
| [9] | Inui H,Oh M H,Nakamura A,Yamaguchi M.Acta Mater,1992; 40:3095 |
| [10] | Rutter J W,Chalmers B.Can J Phys,1953; 31:29 |
| [11] | Hu H Q.Solidification Principle of Metals.Beijing:China Machine Press,2000:130(胡汉起.金属凝固原理.北京:机械工业出版社,2000:130) |
| [12] | Xu Y.Electromagnetism.Nanjing:Jiangsu Science and Technology Press,1987:281(徐游.电磁学.南京:江苏科学技术出版社,1987:281) |
| [13] | Zi B T,Ba Q X,Cui J Z,Bai Y X.Acta Phys Sin,2000;49:1010(訾炳涛,巴启先,崔建忠,白玉先.物理学报,2000;49:1010) |
| [14] | Zhang Q,Ban C Y,Cui J Z,Ba Q X,Lu G M,Zhang B J.Acta Phys Sin,2003; 52:2642(张勤,班春燕,崔建忠,巴启先,路贵民,张北江.物理学报,2003;52:2642) |
| [15] | Shi H F,Xiao L,Liu Q.Nonferrous Met,2004; 56:21(时海芳,肖莉,刘晴.有色金属,2004;56:21) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%