利用共焦激光扫描显微镜原位观察了AISl304不锈钢冷却过程中高温铁素体(δ)→奥氏体(γ)相变的过程及其特征.结果表明,γ相优先在δ晶界处形成;冷却速率影响γ相的生长形态,典型形态分为块状、圆形、树枝状等;"游离"γ枝晶发生粗化,并和周围的γ枝晶聚合;相同冷却条件下,δ晶界处的γ枝晶聚合程度明显高于δ晶粒内部;二次枝晶在冷却过程中粗化,并竞争生长.利用ThermoCalc计算C元素在δ→γ相变过程中的偏析系数,以此求解δ→γ相变数学模型.
参考文献
| [1] | Mark B,Lars H,Reiner K,Willi S,Dieter S.Steel Res,2001;72:484 |
| [2] | Ferry M,Thomson M,Manohar P A.Iron Steel Inst Jpn,2002;42:86 |
| [3] | Allan G K.Ironmaking Steelmaking,1995;22:465 |
| [4] | Liang G F,Wang C Q,Fang Y.Acta Metall Sin,2006;42:708(梁高飞,王成全,方园.金属学报,2006;42:708) |
| [5] | Yin H,Emi T,Shibata H.Acta Mater,1999;47:1523 |
| [6] | Dippenaar R,Phelan D.Metall Mater Trans,2003;34B:495 |
| [7] | Phelan D,Dippenaar R.ISIJ Int,2004;44:414 |
| [8] | Phelan D,Dippenaar R.Metall Mater Trans,2004;35A:3701 |
| [9] | Liang G F,Wang C Q,Fang Y.Acta Metall Sin,2006;42:805(梁高飞,王成全,方园.金属学报,2006;42:805) |
| [10] | Wej Z Y.Iron Steel,1980;15(2):45(魏振宇.钢铁,1980;15(2):45) |
| [11] | Mizoguchi T,Miyazawa K.ISIJ Int,1995;35:771 |
| [12] | Ma Y,Hao Y,Yan F Y,Liu H J.Acta Metall Sin,2001;37:202(马颖,郝远,阎峰云,刘洪军.金属学报,2001;37:202) |
| [13] | Liu Z Y,Fu H z.Chin J Nonferrous Met,1997;7(1):164(刘志义,傅恒志.中国有色金属学报,1997;7(1):164) |
| [14] | He G,Li J G,Mao X M,Fu H Z.J Synth Cryst,1995;24:278(何国,李建国,毛协民,傅恒志.人工晶体学报,1995;24:278) |
| [15] | Liu Z Z,Kobayashi Y,Yang J,Nagai K,Kuwabara M.ISIJ Int.2006;46:847 |
| [16] | Ueshima Y,Mizoguchi S,Matsumiya T,Kajioka H.Metall Trans,1986;17B:845 |
| [17] | Ueshima Y,Sawada Y,Mizoguchi S,Kajioka H.Metall Trans,1989;20A:1375 |
| [18] | Liang G F,Wang C Q,Wu J C,Zhu G M,Yu Y,Fang Y.Acta Metall Sin(Engl Lett),2006;19:441 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%