利用多相场模型,模拟了CBr4-C2Cl6共晶合金定向凝固稳态生长及非稳态变速生长过程.稳态生长模拟结果与Jackson-Hunt共晶理论描述一致,验证了模型的可靠性.非稳态变速生长模拟表明:阶跃增速或减速时,片层间距的调整分别通过突变分叉、或逐步湮没与合并以及自身相的长大方式进行,两者片层间距的选择过程表现为强烈的非对称性;相对于阶跃时刻,片层间距调整、界面平均生长速率与平均过冷度的变化均具有滞后性.
参考文献
[1] | Karma A.Phys Rev,1994;49E:2245 |
[2] | Nestler B,Wheeler A A.Physica,2000;138D:114 |
[3] | Kim S G,Kim W T,Suzuki T,Ode M.J Cryst Growth,2004;261:135 |
[4] | Tiaden J.J Cryst Growth,2004;198/199:1257 |
[5] | Nestler B,Wheeler A A,Ratke L,StScker C.Physica,2000;141D:133 |
[6] | Huang W D,Ding G L,Zhou Y H.Chin J Mater Res,1995;9:193(黄卫东,丁国陆,周尧和.材料研究学报,1995;9:193) |
[7] | Mollard F R,Flemings M C.TMS AIME,1967;239:1526 |
[8] | Seetharaman V,Trivedi R.In:Stefanescu D M,Abbaschian G J,Bayuzick R J,eds.,Solidification Processing of Eutectic Alloys,Warrendale,PA:The Metallurgical Society,1988:65 |
[9] | Apel M,Boettger B,Diepers H J,Steinbach I.J Cryst Growth,2002;237:154 |
[10] | Folch R,Plapp M.Phys Rev,2003;68E:010602 |
[11] | Steinbach I,Pezzolla F.Physica,1999;134D:385 |
[12] | Mergy J,Faivre G,Guthmann C,Mellet R.J Cryst Growth,1993;134:353 |
[13] | Jackson K A,Hunt J D.TMS AIME,1966;236:1129 |
[14] | Ginibre M,Akamatsu S,Faivre G.Phys Rev,1997;56E:780 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%