建立了薄板坯连铸结晶器铜板的三维传热数学模型,特别是对结晶器铜板冷面的水槽和背板部分采用了交替配置不同的边界条件处理,利用Visual Fortran语言自编程序计算结晶器铜板温度场.通过对一典型薄板坯连铸结晶器铜板模拟分析,发现铜板热面温度呈现云层分布,冷面温度呈冰柱状分布.分析了各种工艺参数(拉速、铜板厚度、冷却水流速等)对结晶器铜板温度场的影响,典型位置上的计算结果与现场测量数据符合较好,为优化生产工艺参数和结晶器设计提供理论依据和实际参考数据.
参考文献
| [1] | Samarasekera I V,Brimacombe J K.Trans ISS,1984; 5:79 |
| [2] | Zhang H,Tao H B,Liu A Q,Zhang Z B,Wang J B,Zhuang H Z.Iron Steel,2005; 40(7):25(张慧,陶红标,刘爱强,张振彪,王进步,庄汉洲.钢铁,2005;40(7):25) |
| [3] | Thomas B G,Park J K,Sok Y U.Metall Mater Trans,2002; 33B:425 |
| [4] | Lu M J,Kuo Y Y,Ong T H,Lin C H.Steelmaking Conf Proc,1996; 241:246 |
| [5] | Mahapatra R B,Samarasekera I V,Brimacombe J K.Metall Trans,1991; 22B:861 |
| [6] | Samarasekera I V,Brimacombe J K.Steelmaking Conf Proc,1991; 189:196 |
| [7] | Thomas B G,Li G,Moitra A,Habing D.Ironmaking Steelmaking,1998; 12:125 |
| [8] | Won Y M,Yeo T J,Oh K H,Park J K,Choi J,Yim C H.ISIJ Int,1998; 38:53 |
| [9] | Na X Z,Zhang H,Gan Y,Zhang X Z.Iron Steel (Suppl),2000; 35:233(那贤昭,张慧,干勇,张兴中.钢铁(增刊),2000;35:233) |
| [10] | Thomas B G.Metall Mater Trans,1994; 25B:443 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%