在加入硅烷偶联剂γ-APS的苯胺中性溶液中采用恒电流法在电镀锌钢板上制备聚苯胺膜,采用SEM观测其表面形貌,测试不同条件下聚合膜的厚度.交流阻抗和盐雾实验表明,加入γ-APS后,聚苯胺膜层的致密性和防护性明显提高,接近铬酸盐钝化膜.通过XPS分析,得到γ-APS改性聚苯胺膜掺杂度为11%、氧化度为64%;与改性前聚苯胺膜相比较,掺杂度降低、氧化度增高.结合红外光谱和XPS分析,发现聚苯胺膜中存在4种化学环境:C-Si-O-Si,C-Si-OH,C-Si-O-C,C-Si-O-Zn.
参考文献
| [1] | Rajagopalan R,Iroh J O.Electrochim Acta,2002; 47:1847 |
| [2] | Cascalheira A C,Aeiyach S,Lacaze P C,Arantes L M.Electrochim Acta,2003; 48:2523 |
| [3] | Lacroix J C,Camalet J L,Aeiyach S,Chane-Ching K I,Petitjean J,Chauveau E,Lacaze P C.J Electroanal Chem,2000; 481(1):76 |
| [4] | Yin R H,Zhao Y P,Dai Y C,Zhang X S.Acta Metall Sin,2004; 40:168(印仁和,赵亚萍,戴迎春,张新胜.金属学报,2004;40:168) |
| [5] | Jiang Y F,Guo X W,Zhai C Q,Ding W J.J Funct Polym,2002; 15:473(蒋永峰,郭兴伍,翟春泉,丁文江.功能高分子学报,2002;15:473) |
| [6] | Zhao Y P,Yin R H,Cao W M,Yuan A B.Acta Metall Sin (Engl Lett),2004; 17:849 |
| [7] | Jing X L,Zhao W B.Petro Technol Appl,2001; 19:225(井新利,赵卫兵.石化技术与应用,2001;19:225) |
| [8] | Sun J P,Li B M.Fine Chem,2002; 19:578(孙建平,李宝铭.精细化工,2002;19:578) |
| [9] | Genies E M,Penneau J F,Lapkowski M,Boyle A.J Electroanal Chem,1989; 269(1):63 |
| [10] | Kang E T,Neoh K G,OngY K,Tan K L,Tan B T G.Synth Met,1990; 39:69 |
| [11] | Lei J T,Cai Z H,Martin C R.Synth Met,1992; 46:53 |
| [12] | Zhao Y P.Master Thesis,Shanghai University,2004(赵亚萍.上海大学硕士学位论文,2004) |
| [13] | Huang K L,Liu J S,Liu S Q.J Funct Mater,2000; 31:551(黄可龙,刘建生,刘素琴.功能材料,2000;31:551) |
| [14] | Graupner W.Synth Met,1993; 55-57:3623 |
| [15] | Malinauskas A.Polymer,2001; 42:3957 |
| [16] | Child T F,van Ooij W J.Trans Inst Met Finish,1999,77(2):64 |
| [17] | Plueddemann E P.Silane Coupling Agents.2nd ed,New York:Plenum Press,1991; 227 |
| [18] | Zhu D.PhD Dissertation.University of Cincinnati,Cincinnati,USA,2002 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%