分别采用高温氧化和真空电弧离子镀法在SiC纤维表面制备出C-Al2O3和SiO2-Al2O3复合涂层,通过真空热压法制备出SiCf/Ni复合材料.经过850-950℃,150 h真空热处理后,复合涂层很好地保护了纤维的完整性,涂层中的Al2O3层与基体Ni界面结合良好,有效地阻挡了SiCf/Ni界面处元素互扩散.C-Al2O3涂层的C层出现了扩散现象,但涂层基本保持完整;SiO2-Al2O3涂层中SiO2层与纤维结合界面处萌生裂纹.C-Al2O3与SiO2-Al2O3复合涂层相比具有更好的阻挡界面处元素互扩散的作用.
参考文献
| [1] | Mileiko S T,Kiiko V M,Kolchin A A,Serebryakov A V,Korzhov V P,Starostin M Y,Sarkissyan N S.Compos Sci Technol,2002; 62:167 |
| [2] | Mileiko S T,Kiiko V M,Kolchin A A,Korzhov V P,Prokopenko V M.Compos Sci Technol,2002; 62:181 |
| [3] | Mileiko S T.Compos Sci Technol,2002; 62:195 |
| [4] | Hu W,Karduck P,Gottstein G.Acta Mater,1997; 45:4535 |
| [5] | Zhang W,Smith J R,Evans A G.Acta Mater,2002; 50:3803 |
| [6] | Yu Q,Chen P,Lu C.Insulant Mater,2005; 2:50(于祺,陈平,陆春.绝缘材料,2005;2:50) |
| [7] | Cai S,Li Z Y,Dong Y,Yan M G.J Aeronaut Mater,2006;26(2):22(蔡杉,李占一,董妍,颜鸣皋.航空材料学报,2006;26(2):22) |
| [8] | Feng C X,Xue J G,Song Y C.Hi Tech Fiber Appl,2003;28(1):15(冯春祥,薛金根,宋永才.高科技纤维与应用,2003;28(1):15) |
| [9] | Yu Y X,Cao F,Li X D.Acta Mater Compos Sin,2004;21(5):79(余煜玺,曹峰,李效东.复合材料学报,2004;21(5):79) |
| [10] | Tang W M,Zheng Z X,Ding H F,Jin Z H.J Chin Ceram Soc,2003; 31:287(汤文明,郑治祥,丁厚福,金志浩.硅酸盐学报,2003;31:287) |
| [11] | Li R J.Ceramic Metal Composite.Beijing:Metallurgical Industry Press,2004,99(李荣久.陶瓷-金属复合材料.北京:冶金工业出版社,2004,99) |
| [12] | Mittncki M A.SAMPE,1990; 26(5):49 |
| [13] | Feng Z D,He L Z,Wang Y Y.Phys Chem Insp-Phys Fasc,2005; 41(Suppl.):59(冯祖德,何立志,王艳艳.理化检验-物理分册,2005;41(增刊):59) |
| [14] | Zheng C M,Li X D,Wang Y F,Wang Y D,Feng C X.Aerosp Mater Technol,2005; 35(3):7(郑春满,李效东,王亦菲,王应德,冯春祥.宇航材料工艺,2005;35(3):7) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%