利用激光熔化沉积技术制备了AerMet 100耐蚀超高强度钢薄壁板状试样.结果表明,试样具有细小均匀、无侧向分枝的快速凝固胞状组织及优异的力学性能,其室温下的纵向和横向抗拉强度分别达到1464和1402 MPa,延伸率分别达到20.3%和29.7%.讨论了往复式扫描激光熔化沉积过程中"之"字形胞状组织的凝固过程,并建立了基于胞晶择优外延生长的物理模型.
参考文献
| [1] | Novotny P M,Maguire M.Foundry Managem Technol,1993;121(12):33 |
| [2] | Hemphill R M.Steel Times,1995;223(5):191 |
| [3] | Dahl J M,Novotny P M.Adv Mater Processes,1999;155(3):23 |
| [4] | Garrison W M.JOM,1990;42(5):20 |
| [5] | Wang H M,Zhang L Y,Li A,Cai L X,Tang H B,Lu X D.World Sci-Technol R D,2004;26(3):27(王华明,张凌云,李安,蔡良续,汤海波,吕旭东.世界科技研究与发展,2004;26(3):27) |
| [6] | Wang H M,Zhang L Y,Li A,Cai L X,Tang H B.J Beijing Univ Aeronaut Astronaut,2004;30:962(王华明,张凌云,李安,蔡良续,汤海波.北京航空航天大学学报,2004;30:962) |
| [7] | Gaumann M,Henry S,Cleton F,Wagniere J D,Kurz W.Mater Sci Eng,1999;A271:232 |
| [8] | Abbott D H.Met Powder Rep,1998;53(2):24 |
| [9] | Abbott D H,Arcella F G.Adv Mater Processes,1998;153(5):29 |
| [10] | Chang C E,Wilcox W R.J Cryst Growth,1974;21:35 |
| [11] | Yang S,Huang W D,Liu W J,Su Y P,Zhou Y H.Acta Metall Sin,2001;37:571(杨森,黄卫东,刘文今,苏云鹏,周尧和.金属学报,2001;37:571) |
| [12] | Liu Z Y,Li J G,Fu H Z.Acta Metall Sin,1995;31:329(刘忠元,李建国,傅恒志.金属学报,1995;31:329) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%