采用微生物法和化学沉积法在直径为0.4-0.6μm的诺卡氏(Nocadia)菌体表面成功沉积了厚度约为200 nm、晶粒尺寸约为20 nm的Cu镀层,制备出新型Cu微米杆材料.在相同条件下,十二烷基苯磺酸钠对菌体的分散效果好于焦磷酸钠.在表面活性剂十二烷基苯磺酸钠和机械搅拌联合分散下,菌体均匀分散在前处理溶液和镀铜液中.施镀过程中,菌体保持原有形状,得到了纳米Cu晶粒组成的微米级杆状金属材料.
参考文献
| [1] | Zhang D Y,Li Y Q.In:Yang H Y,Li W,eds.,4th Int Conf on Frontiers of Design and Manufacturing,Beijing:International Academic Publishers,2000:17 |
| [2] | Sleytr U B,Messner P,Sara M,Pum D.Syst Appl Microb.1986;7:301 |
| [3] | Shenton W,Pum D,Sleytr U B,Mann S.Nature,1997:389:585 |
| [4] | Whaley S R,English D S,Hu E L,Barbara P F.Belcher A M.Nature.2000;405:665 |
| [5] | Lee S W,Mao C B,Flynn C E,Belcher A M.Science.2002;296:892 |
| [6] | Matsui H,Gologan B.J Phys Chem,2000;104B:3383 |
| [7] | Matsui H,MacCuspie R.Nano Lett,2001:1:671 |
| [8] | Matsui H,Porrata P,Douberly G E.Nano Lett.2001:1:461 |
| [9] | Li X F,Li Y Q,Cai J,Zhang D Y.Sci Chin,2003;46E:161 |
| [10] | Li X F,Li Y Q,Cai J,Zhang D Y.Chin Sci Bull,2003:48:145(黎向锋,李雅芹,蔡军,张德远.科学通报,2003;48:145) |
| [11] | Cai J,Li Y Q,Li X F,Zhang D Y.J Magn Magn Mater.2002;246:36 |
| [12] | Tay B Y,L.Liu,Loh N H,Tor S B,Murakoshi Y,Maeda R.Mater Character,2006;57(2):80 |
| [13] | Zhang Y S,Wang L S,Liu X H,Yan Y J,Chen C Q,Zhu J.J Phys Chem,2005;109B:13091 |
| [14] | Zhang S G,Marini D M,Hwang W,Santoso S.Curr Opin Chem Biology,2002;6:865 |
| [15] | Hu C X.Handbook of Surface Pre-Processing in Practice.Beijing:Chemical Industry Press,2003:392(胡传忻.实用表面前处理处理手册.北京:化学工业出版社,2003:392) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%