通过粘接低熔点合金后拉伸,可使纯铁表面氢鼓泡被剖开,露出内部断口形貌.扫描电镜观察和能谱分析表明,氢鼓泡是含H2的空腔,大多数(88%)鼓泡核附近存在夹杂.这表明含H2空腔择优在夹杂界面处形成.当鼓泡中氢压产生的应力超过原子键合力(有可能被氢降低)时,裂纹从鼓泡核壁形成,产生断裂花样,氢进入已开裂的鼓泡就使它通过裂纹扩展而不断长大,直至鼓泡破裂,内部氢压释放.
参考文献
| [1] | Zaffe C A,Sims C E.Trans AIME,1941;145:225 |
| [2] | Hirth J P.Metall Trans,1980;11A:861 |
| [3] | Chen L,Xu Y B,Yin W Q.Acta Metall Sin,1978;14:253(陈廉,徐永波,尹万全.金属学报,1978;14:253) |
| [4] | Garofalo F,Chou Y T,Ambegaokar V.Acta Metall,1960;8:504 |
| [5] | Tetelman A S,Robertson W D.Acta Metall,1963;11:415 |
| [6] | Matsui H,Kimura H,Kimura A.Mater Sci Eng,1979;40:227 |
| [7] | Li X G,Dong C F,Li M.J Univ Sci Technol Beijing,2002;9:130 |
| [8] | Wilde B E,Kim C D,Phelps E H.Corrosion,1980;36:625 |
| [9] | Domizzi G,Anteri G,Ovejero-Garcia J.Corros Sci,2001;43:325 |
| [10] | Chu W Y,Gao K W,Huang Y Z,Qiao L J.Corrosion,2000;56:1046 |
| [11] | McLellan R B,Xu Z R.Scr Mater,1997;36:1201 |
| [12] | Gavriljuk V G,Bugaev V N,Petrov Y N,Yanchitski B Z.Scr Mater,1996;34:903 |
| [13] | Iida T,Yamazaki Y,Kobayashi T,Iijima Y,Fukai Y.Acta Mater,2005;53:3083 |
| [14] | Fukai Y,Okuma N.Phys Rev Lett,1994;73:1640 |
| [15] | Morishita K,Sugano R,Wirth B D.J Nucl Mater,2003;323:243 |
| [16] | Daw M S,Baskes M I.Phys Rev,1984,29B:6443 |
| [17] | Garet M,Brass A M,Haut C.Corros Sci,1998;40:1073 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%