采用旋转弯曲疲劳实验研究了含钒的38MnVS钢与不含钒的38MnS钢在热锻态和退火态下的疲劳行为.结果表明,V元素主要通过析出强化和组织细化改善铁素体+珠光体型非调质钢的疲劳性能.在热锻态,V(C,N)呈细小弥散分布,与铁素体间具有特定位向关系,具有明显的析出强化和细化组织作用.铁索体的强化使得疲劳裂纹萌生和扩展的抗力提高,因而38MnVS钢的疲劳性能明显优于38MnS钢;在退火态,V(C,N)质点长大,与铁素体间失去共格关系,不再具有明显的析出强化作用,因而退火态38MnVS钢的疲劳性能明显低于热锻态,而与38MnS钢的疲劳性能相当.
参考文献
| [1] | Dong C R,Ren H P,Jin T Z.MicroaUoyed Non-quenched and Tempered Steels.Beijing:Metallurgical Industry Press,2000:27(董成瑞,任海鹏,金同哲.微合金非调质钢.北京:冶金工业出版社,2000:27) |
| [2] | Engineer S,Huehtemann B,Schuler V.Mater Technol,1987;58:369 |
| [3] | Naylor D J.Ironmaking Steelmaking,1989;16:246 |
| [4] | Inoue T,Katsumata M.J Heat Treat,1993;33:11(井上毅,滕亦正昭.热处理,1993;33(1):11) |
| [5] | Cristinacce M,Reynolds P E.In:Van Tyne C J,Krauss G,Matlock D K eds,Fundamentals and Applications of Microalloying Forging Steels,Warrendale,PA:TMS,1996:29 |
| [6] | Dini G,Vaghefi M M,Shafyei A.ISIJ Int,2006;46(1):89 |
| [7] | Niwa S,Machid I,Kato T,Uyehara N,Tanaka Y.SAE Technical Report,No.810426 |
| [8] | Inoue K,Nakamura S.In:Van Tyne C J,Krauss G,Matlock D K eds,Fundamentals and Applications of Microalloying Forging Steels,Warrendale,PA:TMS,1996:345 |
| [9] | Inoue K,Nakamura S.J Electr Steel Making,1994;65(1):22(井上幸一郎,中村真行.电气制钢,1994;65(1):22) |
| [10] | Nomura I.J Heat Treat,1999;39:289(野村一卫.热处理,1999;39(6):289) |
| [11] | Toyama K.CAMP-ISIJ,2002;15:491 |
| [12] | Zhang J M,Li s X,Yang Z G,Li G Y,Hui W J,Wen Y Q.Int JFatigue,2007,in press |
| [13] | Sawai T,Matsuoka S,Tsuzaki K.Tetsu-Hagane,2003;89(6):104(泽井达明,松冈三郎,津崎兼彰.铁と钢,2003;89(6):104) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%