采用高速电弧喷涂技术制备了含有非晶相的3种铁基涂层(AC1-Fe59.5Cr16.2WC3.0Mn0.3 B20.2Si0.6,AC2-Fe59.8Cr16.0WC1.5Mo1.5Mn0.3B20.0Si0.7,AC3-Fe59.9Cr16.0Sn3.0Mn0.3B20.0C0.2Si0.6).对涂层的极化行为和交流阻抗行为进行了研究,涂层AC1中含有较多的非晶相,在Tafel线性极化区具有最低的自腐蚀电流,在阳极极化时表现出钝化趋势.涂层的电化学阻抗谱均可采用R(Q(R(QR)))型等效电路来进行分析,涂层AC1与其它涂层相比具有更大的电化学反应电阻.在一系列的电化学反应实验中,涂层AC1的耐蚀性最好.
参考文献
| [1] | Zhao Y H,Luo C Y,Xi X K,Zhao D Q,Pan M X,Wang W H.Intermetallics.2006;14:1107 |
| [2] | Stoica M,Eckert J,Roth S,Zhang Z F,Schultz L,Wang W H.Intermetallics.2005;13:764 |
| [3] | Pang S J,Zhang T,Asami K,Inoue A.Acta Mate5 2002;50:489 |
| [4] | Shen T D,Schwarz R B.Acta Mater,2001;49:837 |
| [5] | Afonso C R M,Bolfarini C,Kiminami C S,Bassim N D,Kaufman M J,Amateau M F,Eden T J,Galbraith J M.J Non-Cryst Solids,2001;284:134 |
| [6] | Wiedemann R,Weihnacht V,Oettel H.Surf Coat Technol,1999;116:302 |
| [7] | Yue T M,Su Y P,Yang H O.Mater Lett,2007;61:209 |
| [8] | Sordelet D J,Besser M F.Mater Sci Eng,2004;A375-377:625 |
| [9] | Otsubo F,Era H,Kishitake K.J Therm SPray Technol,2000;4:494 |
| [10] | Kim H J,Lim K M,Seong B G,Park C G.J Mater Sci,2001;36:49 |
| [11] | Verdon C,Karimi A,Martin J L.Mater Sci Eng,1998;A 246:11 |
| [12] | Cerqueiraa M F,Ferreiraa J A,Adriaenssen G J.Thin Solid Films.2000;370:128 |
| [13] | Guo J H,Lu C W,Ni X J,WU J W,Lu Z C,Lian F Z.Chin Surf Eng,2006;19(5):45(郭金花,陆曹卫,倪晓俊,吴嘉伟,卢志超,连法增.中国表面工程,2006;19(5):45) |
| [14] | Cao C N,Zhang J Q.An Introduction to Electrochemical Impedance Spectroscopy.Beijing:Science Press,2002:26(曹楚南,张鉴清.电化学阻抗谱导论.北京:科学出版社,2002:26) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%