通过分析2.0 m/min拉速稳定浇铸时振动周期内弯月面初凝坯壳的受力情况,阐述了高拉速连铸坯表面振痕形成过程,给出振动参数与最大液体摩擦力和最大保护渣渣道动态压力关系;结合振动参数对振动过程参数的影响和实际设备状况,提出了振动参数优化方向,确定了拉速升至2.2 m/min时的振动参数值.结果表明,弯月面初凝坯壳在钢水静压力、摩擦力和保护渣渣道压力作用下随凝固进程形成振痕,振痕生成位置取决于初凝坯壳糊状区固相分率;随拉速提高,应降低振频、增大振幅和非正弦振动因子,以改善振动效果和振痕形貌;拉速升至2.2 m/min时的适宜振频、振幅和非正弦振动因子分别为145 min-1,±5.0 mm和0.25.
参考文献
| [1] | Takeuchi E,Brimacombe J K.Metall Trans,1985; 16B:605 |
| [2] | Lei Z S,Ren Z M,Zhang B W,Deng K.Acta Metall Sin,2002; 38:877(雷作胜,任忠鸣,张邦文,邓康.金属学报,2002;38:877) |
| [3] | Schwerdtfeger K,Sha H.Metall Mater Trans,2000; 31B:813 |
| [4] | Badri A,Natarajan T T,Snyder C C,Powers K D,Mannion F J,Byrne M,Cramb A W.Metall Mater Trans,2005; 36B:373 |
| [5] | Takeuchi E,Brimacombe J K.Metall Trans,1984; 15B:493 |
| [6] | Suzuki M,Mizukami H,Kitagawa T,Kawakami K,Uchida S,Komatsu Y.ISIJ Int,1991; 31:254 |
| [7] | Zhu L G,Wang S M,Jin S T.J Univ Sci Technol Beijing,1999; 21:13(朱立光,王硕明,金山同.北京科技大学学报,1999;21:13) |
| [8] | Meng X N,Zhu M Y,Liu X D,Cheng N L,Jiang Z K.Acta Metall Sin,2007; 43:205(孟祥宁,朱苗勇,刘旭东,程乃良,江中块.金属学报,2007;43:205) |
| [9] | Zhang J M,Zhang L,Wang X H,Wang L F.Acta Metall Sin,2003; 39:1285(张炯明,张立,王新华,王立峰.金属学报,2004;39:1285) |
| [10] | Bikerman J J.Physical Surfaces.London:Academic Press,1970:12 |
| [11] | Cramb A W,Jimbo I.Steel Res,1989; 60:157 |
| [12] | Meng X N,Zhu M Y.Chin J Process Eng,2006;6(Suppl.1):91(孟祥宁,朱苗勇.过程工程学报,2006;6(增刊1):91) |
| [13] | Meng X N,Zhu M Y.Chin Mech Eng,in press(孟祥宁,朱苗勇.中国机械工程,待发表) |
| [14] | Szekeres E S.Iron Steel Eng,1996; 73:29 |
| [15] | Meng X N,Zhu M Y.J Iron Steel Res,in press(孟祥宁,朱苗勇.钢铁研究学报,待发表) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%