通过对连铸板坯的轻压下过程分析,导出了求解铸坯压下率的理论模型,并考察了不同拉速下板坯压下率的变化规律.结果表明,压下率在轻压下入口处最大,沿拉坯方向线性减少;拉速每增加0.2 m/min,平均压下率减少约0.04 mm/m;压下速率的取值范围不受拉速影响,最大值为0.36 mm/min,最小值为0.22 mm/min;压下速率沿拉坯方向呈线性减少,拉速越大,压下速率减少越慢;平均压下速率也不随拉速变化,保持定值0.29 mm/min.
参考文献
| [1] | Sivesson P,Hallen G,Widell B.Ironmaking Steelmaking,1998; 25:239 |
| [2] | Raja V R,Pal N,Jayaswal N P.Steel Times Int,2005;29(4):41 |
| [3] | Scholes A.Ironmaking Steelmaking,2005; 32:101 |
| [4] | Flemings M C.ISIJ Int,2000; 40:833 |
| [5] | Yim C H,Park J K,You B D,Yang S M.ISIJ Int,1996;36(Suppl.):231 |
| [6] | Morwald K,Thalammer M,Federspiel C,Gould L.Steel Times Int,2003; 12(1):17 |
| [7] | Morsut L.MPT Int,2003; 26(2):44 |
| [8] | Heinz H,Manfred T,Michael S,Oliver S,Lawrence G.MPT Int,2003; 26(3):74 |
| [9] | Shigeaki O,Masayuki K,Mamoru Y,Tatsuo M.ISIJ Int,1991; 31:1400 |
| [10] | Ralph N,Karl-Heinz S.Steel Res,2003; 74:700 |
| [11] | Yamanaka A,Okuda M.Ironmaking Steelmaking,1999;26:64 |
| [12] | Chen S Q,Zhang J Q,Cui L X,Gan Y,Ni M S.J Iron Steel Res,2003; 15(2):9(陈素琼,张家泉,崔立新,干勇,倪满森.钢铁研究学报,2003;15(2):9) |
| [13] | Chen Q A,Li Z L,Wang L Z,Wang J W.Iron Steel,2001;36(9):38(陈其安,李振亮,王连仲,王建伟.钢铁,2001;36(9):38) |
| [14] | Lin Q Y.Master Thesis,Northeastern University,Shenyang,2004(林启勇.东北大学硕士学位论文,沈阳,2004) |
| [15] | Ito Y,Yamanaka A,Watanabe T.Rev Metall,2000; 97:1171 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%