通过XRD和磁性测量对非化学计量比MnFe(P,Si,Ge)合金的相组成和磁性进行了研究.XRD分析表明,所有样品都具有Fe2P型六角结构,主相为(Fe,Mn)2(P,Si,Ge),并存在少量的第二相(Fe,Mn)3(Si,Ge).过量的Mn和Fe都会使合金的Curie温度降低,由343 K(化学计量比)降低到294 K(过量Mn)和286 K(过量Fe);过量的Mn能减小热滞,而过量的Fe会使热滞增加;磁熵变也有所减小,在1.5 T的磁场下,最大磁熵变由5.2 J/(kg·K)(化学计量比)减小到4.9 J/(kg·K)(过量Mn)和3.8 J/(kg·K)(过量Fe).
参考文献
| [1] | Tegus O,Brück E,Buschow K H J,de Boer F R.Nature,2002; 415:150 |
| [2] | Pecharsky V K,Gschneidner J K A.Phys Rev Lett,1997;78:4494 |
| [3] | Brück E,Tegus O,Zhang L,Li X W,de Boer F R,Buschow K H J.J Alloys Compd,2004; 383:32 |
| [4] | Tegus O,Fuquan B,Dagula W,Zhang L,Brück E,Si P Z,de Boer F R,Buschow K H J.J Alloys Compd,2005;396:6 |
| [5] | Dagula W,Tegus O,Li X W,Song L,Brück E,Cam Thanh D T,de Boer F R,Buschow K H J.J Appl Phys,2006; 99:08Q105 |
| [6] | Brück E,Ilyn M,Tishin A M,Tegus O.J Magn Magn Mater,2005; 290-291:8 |
| [7] | Tegus O,Brück E,Li X W,Zhang L,Dagula W,de Boer F R,Buschow K H J.J Magn Magn Mater,2004; 272-276:2389 |
| [8] | Teg us O,Brück E,Zhang L,Dagula W,Buschow K H J,de Boer F R.Physica,2002; 319B:174 |
| [9] | Brück E,Tegus O,Li X W,de Boer F R,Buschow K H J.Physica,2003; 327B:431 |
| [10] | Zener C.Phys Rev,1951; 82:403 |
| [11] | Millis A J,Littlewood P B,Shraiman B I.Phys Rev Lett,1995; 74:5144 |
| [12] | Zhang L.PhD Dissertation,University of Amsterdam,2005 |
| [13] | Bacmann M,Soubeyroux J L,Barrett R.J Magn Magn Mater,1994; 134:59 |
| [14] | McGuire T R,Gupta A,Duncombe P R.J Appl Phys,1996; 79:4549 |
| [15] | Dionne G F.J Appl Phys,1996; 79:172 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%