基于电子背散射分析(EBSD)技术对纯铜柱状晶标定获得的初始晶粒形貌和平均取向,利用晶体塑性理论,建立了基于晶粒真实取向和形貌的多晶塑性有限元模型,模拟了纯铜柱状晶单轴压缩过程中的取向变化,并对形变带形貌进行初步模拟.通过相应的单轴压缩实验获得了取向变化和形变带形貌的实验数据.系统地比较了多晶样品中各晶粒取向演化和形变带形貌的模拟结果和实验结果,得到晶粒取向和微观结构变化的统计性结果.
参考文献
[1] | Taylor G I.J Inst Met,1938; 62:307 |
[2] | Sachs G.Z Ver Deut Ing,1928; 72:734 |
[3] | Bronkhorst C A,Kalidindi S R,Anand L.Philos Trans R Soc London,1992; 341:443 |
[4] | Kalidindi S R,Bronkhorst C A,Anand L.J Mech Phys Solids,1992; 40:537 |
[5] | Peirce D,Asaro R J,Needleman A.Acta Metall,1982; 30:1087 |
[6] | Wu P D,Neale K W,van der Giessen E.Int J Plast,1996;12:1199 |
[7] | Delannay L,Kalidindi S R,van Houtte P.Mater Sci Eng,2002; A336:233 |
[8] | Delannay L,Loge R E,Chastel Y,Van Houtte P.Acta Mater,2002; 50:5127 |
[9] | Van Houtte P,Delannay L,Kalidindi S R.Int J Plast,2002; 18:359 |
[10] | Dong X H,Zheng Y,Li Z G.Chin Mech Eng,2003; 15:1339(董湘怀,郑莹,李志刚.中国机械工程,2003;15:1339) |
[11] | Bhattacharyya A,El-Danaf E,Kalidindi S R,Doherty R D.Int J Plast,2001; 17:861 |
[12] | Panchanadeeswaran S,Doherty R D,Becker R.Acta Mater,1996; 44:1233 |
[13] | Raabe D,Sachtleber M,Zhao Z,Roters F,Zaefferer S.Acta Mater,2001; 49:3433 |
[14] | Delannay L,Jacques P J,Kalidindi S R.Int J Plast,2006;22:1879 |
[15] | Deng Y L,Zhang X M,Tang J G,Liu Y,Chen Z Y,Zhou Z P.Acta Metall Sin,2005; 41:477(邓运来,张新明,唐建国,刘瑛,陈志勇,周卓平.金属学报,2005;41:477) |
[16] | van Houtte P,Li S,Seefeldt M,Delannay L.Int J Plast,2005; 21:589 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%