研究了低频电磁铸造和普通DC铸造7050铝合金铸锭经挤压变形后所得板材制品的微观组织及时效特性.结果表明,低频电磁铸锭挤压板材的微观组织保持了其原始铸态组织晶粒细小的特点.在相同挤压比条件下,低频电磁铸锭挤压板的平均晶粒直径约为10 μm,而普通DC铸锭挤压板的平均晶粒直径约为20 μm.低频电磁铸锭挤压板具有更快的时效强化速率和更好的时效强化效果.两种挤压板在120℃进行单级时效时,低频电磁铸锭挤压板经8 h达到强度峰值,其纵向和横向的拉伸强度分别为656和596 MPa;而普通DC铸锭挤压板经12 h才达到强度峰值,其纵向和横向的拉伸强度分别为647和590 MPa.
参考文献
| [1] | Zhang B J,Cui J Z.Mater Sci Eng,2003; A355:325 |
| [2] | Zhang B J,Cui J Z,Lu G M,Zhang Q,Ban C Y.Acta Metall Sin,2002; 38:215(张北江,崔建忠,路贵民,张勤,班春燕.金属学报,2002;38:215) |
| [3] | Zhang B J,Cui J Z,Lu G M.Mater Lett,2003; 57:1707 |
| [4] | Dong J,Cui J Z.Metall Mater Trans,2004; 35A:2487 |
| [5] | Dong J,Liu X T,Zhao Z H,Bao W P,Cui J Z.Acta Metall Sin,2004; 40:215(董杰,刘晓涛,赵志浩,包卫平,崔建忠.金属学报,2004;40:215) |
| [6] | Zuo Y B,Cui J Z,Dong J,Yu F X.J Alloy Compd,2005;402:149 |
| [7] | Zuo Y B,Cui J Z,Dong J.Mater Sci Eng,2005; A408:176 |
| [8] | Vives C.Metall Trans,1989; 20B:623 |
| [9] | Dong J,Cui J Z,Zeng X Q,Ding W J.Mater Lett,2005;59:1502 |
| [10] | Jia F,Jin J Z.Acta Metall Sin,2002; 38:393(贾非,金俊泽.金属学报,2002;38:393) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%