研究了强磁场与交变电流复合作用产生的振荡对Al-18%Si合金中初生硅分布和形貌的影响规律.结果表明,磁场强度较小时,初生硅发生偏聚现象;随着磁场强度的增大(10 T),初生硅的偏聚现象逐渐减小至消失,并且随着振荡力的增大,初生硅由星瓣状向板条状和近颗粒状转变.同时,分析了初生硅的迁移行为,发现磁场下颗粒迁移的终端速度随颗粒尺寸的减小以及磁场强度的增大而降低.理论分析与实验结果相符.
参考文献
| [1] | David P.Mod Cast,1990; 82(2):55 |
| [2] | Pan E N,Hu J F.AFS Trans,1998; 105:413 |
| [3] | Bunk W G.Mater Sci Eng,1991; A134:1087 |
| [4] | Vives C.Mater Sci Eng,1993; A173:169 |
| [5] | Vives C.J Cryst Growth,1996; 158:118 |
| [6] | Radjai A,Miwa K,Nishio T.Metall Mater Trans,1998;29A:1477 |
| [7] | Radjai A,Miwa K,Nishio T.Metall Mater Trans,2002;33A:3025 |
| [8] | Takagi T,Iwai K,Asai S.ISIJ Int,2003; 43:842 |
| [9] | Iwai K,Sugiura K.Mater Sci Forum,2005; 475:2695 |
| [10] | Wang H L,Ren Z M,Ren W L,Wang J,Deng K,Zhong Y B.Shanghai Met,2006; 28(5):40(王洪亮,任忠鸣,任维丽,王俊,邓康,钟云波.上海金属,2006;28(5):40) |
| [11] | Ren W L,Ren Z M,Wang H L,Zhong Y B,Deng K,Yu J B.Mater Sci Technol,in press(任维丽,任忠鸣,王洪亮,钟云波,邓康,余建波.材料科学与工艺,待发表) |
| [12] | Wang J,Deng K,Ren Z M,Ren W L,Li X,Zhong Y B,Xu K D.Shanghai Met,2006; 28(6):7(王俊,邓康,任忠鸣,任维丽,李喜,钟云波,徐匡迪.上海金属,2006;28(6):7) |
| [13] | Zhang Q,Cui J Z.Chin J Nouferrous Met,2003; 13:1500(张勤,崔建忠.中国有色金属学报,2003;13:1500) |
| [14] | Mao W M,Li S S,Zhao A M,Cui C L,Zhong X Y.Mater Sci Technol,2001; 9:117(毛为民,李树索,赵爱民,崔成林,钟雪友.材料科学与工艺,2001; 9:117) |
| [15] | Zhang B W.PhD Dissertation,Shanghai University,2003:26(张邦文.上海大学博士学位论文,2003:26) |
| [16] | Zhou Y H,Hu Z Q,Jie W Q.Solidification Technology.Beijing:China Machine Press,1998:46(周尧和,胡壮麒,介万奇.凝固技术.北京:机械工业出版社,1998:46) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%