利用X射线四轴衍射仪测定了四点弯曲弹性加载条件下镍基单晶高温合金表层的宏观应变与应力,并与应变片及机械拉伸测定的数据进行了比较.分析了采用不同弹性常数及不同分峰方式处理得到的应力数据的差异.结果表明,实验数据重复性较好,实验误差为±30 MPa;XRD测量得出的应力应变结果与室温拉伸以及应变片测量结果符合较好;室温下合金基体相(γ)的弹性常数大于沉淀强化相(γ'),且基体相(γ)承受的应力大于沉淀强化相(γ').
参考文献
[1] | Ganghoffer J F,Hazotte A,Denis S,Simon A.Scr Metall Mater,1991; 25:2491 |
[2] | Muller L,Glatzel U,Fellerkniepmeier M C.Acta Metall Mater,1993; 41:3401 |
[3] | Kuhn H A,Biermann H,Ungar T,Mughrabi H.Acta Metall Mater,1991; 39:2783 |
[4] | Biermann H,Tetzlaff U,von Grossmann B,Mughrabi H,Schulze V.Scr Mater,2000; 43:807 |
[5] | Wang Q M,Li H,Guo M H,Ke P L,Gong J,Sun C,Wen L S.Mater Sci Eng,2005; A406:350 |
[6] | Lu Z,Pyczak F,Biermann H,Mughrabi H.Philos Mag,2002; 82A:1219 |
[7] | Von Grossmann B,Biermann H,Tetzlaff U,Pyczak F,Mughrabi H.Scr Mater,2000; 43:859 |
[8] | Ortner B J.Appl Cryst,2005; 38:678 |
[9] | Hecker M,Thiele E,Holste C.Acta Mater,2002; 50:2357. |
[10] | Suzuki H,Akita K,Misawa H.Jpn J Appl Phys (Part 1),2003; 42(5A):2876 |
[11] | Yoshioka Y,Ohya S,Suyama Y.ICRS-5,1997:528 |
[12] | Marty B,Moretto P,Gergaud P,Lebrun J L,Ostolaza K,Ji V.Acta Mater,1997; 45:791 |
[13] | Durand L,Massaoudi M,Lavelle B.Mater Des,2005; 26:402 |
[14] | Eberl F,Lebrun J L,Cailletaud G.Adv X-ray Anal,2000;42:528 |
[15] | Winholtz RA,Cohen J B.Mater Sci Eng,1992; A154:155 |
[16] | Ichitsubo T,Koumoto D,Hirao M,Tanaka K,Osawa M,Yokokawa T,Harada H.Acta Mater,2003; 51:4863 |
[17] | Ma S,Rangaswamy P,Majumdar B S.Scr Mater,2003;48:525 |
[18] | Hunter B A,Howard C J.ANSTO report,1998 |
[19] | Muller L,Glatzel U,Fellerkniepmeier M.Acta Metall Mater,1992; 40:1321 |
[20] | Gayda J,MacKay R A.Scr Metall,1989; 23:1835 |
[21] | Yamashita M,Kakehi K.Scr Mater,2006; 55:139 |
[22] | Kakehi K.Scr Mater,1999; 41:461 |
[23] | Sondhi S K,Dyson B F,McLean M.Acta Mater,2004;52:1761 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%