采用区熔定向凝固技术制备了〈110〉取向(Tb0.36Dyo.64)1-xHoxFe2合金,研究了在0,5和10 MPa压力下该合金的磁致伸缩性能及其磁致伸缩的滞后特性.结果表明:在外加轴向压应力作用下,〈110〉取向(Tb0.36Dy0.64)1-xHoxFe2合金具有明显的磁致伸缩"跳跃效应";x＜0.3的合金在较宽的温度范围(-60-80℃)内具有巨磁致伸缩特性;随x的增加,合金磁致伸缩滞后显著降低.在外加压力为0,5和10 MPa时,相对于滞后宽度为10.4,13.5和16.6 kA/m的x=0合金而言,x=0.1合金的滞后宽度减小为9.3,11.6和13.7 kA/m;x=0.2合金的滞后宽度减小为7.5,10.8和12.9 kA/m;x=0.3合金的滞后宽度减小为5.4,8.8和9.8 kA/m.
参考文献
| [1] | Clark A E.Ferromagnetic Materials.Vol.1,Amsterdam:North-Holland,1980:531 |
| [2] | Anjanappa M,Wu Y.Smart Mater Struct,1997; 6:393 |
| [3] | Tang C C,Du J,Li Y X,Wang F W,Wu G H,Zhan W S,Qu J P.Appl Phys Lett,1998; 73:692 |
| [4] | Funayama T,Kobayashi T,Sakai I,Sahashi M.Appl Phys Lett,1992; 61:114 |
| [5] | Ma T Y,Jiang C B,Xu H B.J Alloys Compd,2005; 388:34 |
| [6] | Wun-Fogle M,Restorf J B,Clark A E,Lindberg J F.J Appl Phys,1998; 83:7279 |
| [7] | Wun-Fogle M,Restorf J B,Clark A E.J Appl Phys,2000;85:6253 |
| [8] | Busbridge S C,Piercy A R.IEEE Trans Magn,1995; 31:4044 |
| [9] | Jiang C B,Zhao Y,Xu H B.Acta Metall Sin,2004; 40:373;(蒋成保,赵岩,徐惠彬.金属学报,2004;40:373) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%