采用Potts模型Monte Carlo方法对3种现存的三维个体晶粒长大速率拓扑依赖性方程进行了仿真验证.结果表明,Rivier速率方程认为晶粒体积变化率dVf/dt与晶粒面数,成线性关系,与仿真结果明显不符,不适用于描述三维晶粒长大过程的动力学.当晶粒面数f≥8时,Yu-Liu速率方程和MacPherson-Srolovitz速率方程均与仿真结果很好吻合,表明这两者均可以用来定量描述三维晶粒长大过程的动力学;当f<8时,这两个方程均与仿真结果有显著差异.
参考文献
| [1] | Beck P A,Holaworth M L,Hu H.Phys Rev,1948; 73:526 |
| [2] | Burke J E.Trans AIME,1949; 180:73 |
| [3] | Turnbull D.Trans AIME,1951; 191:661 |
| [4] | von Neumann J.In:Herring C,ed.,Metal Interlaces,Cleveland,American Society for Metals,1952:108 |
| [5] | Mullins W W.In:Robertson W D,Gjostein N A,eds.,Metal Surfaces:Structure,Energetics,and Kinetics,Met-als Park,OH:American Society for Metals,1963:17 |
| [6] | Mullins W W.J Appl Phys,1956; 27:900 |
| [7] | Rivier N.Philos Mag,1983; 47B:245 |
| [8] | Yu H B,Liu G Q.Chin Sci Bull,1996; 41:2000(王超,刘国权,于海波.金属学报,2004;40:1233) |
| [9] | Liu G Q,Yu H B,Song X Y,Qin X G.Mater Des,2001;22:33 |
| [10] | Liu G Q,Song X Y,Yu H B,Gu N J.Acta Metall Sin,1999; 35:245(于海波,刘国权.科学通报,1996;41:2000) |
| [11] | Wang C,Liu G Q,Yu H B.Acta Metall Sin,2004; 40:1233(刘国权,宋晓艳,于海波,谷南驹.金属学报,1999;35:245) |
| [12] | MacPherson R D,Srolovitz D J.Nature,2007; 446:1053 |
| [13] | Qin X G.Doctorate Dissertation,University of Science and Technology Beijing,2003(秦湘阁.北京科技大学博士学位论文,2003) |
| [14] | Glazier J A.Phys Rev Left,1993; 70:2170 |
| [15] | Radhakrishnan B,Zacharia T.Metall Mater Trans,1995;26A:167 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%