研究了不同熔体超温处理温度对DD3单晶高温合金二次枝晶间距的影响,并利用旋转定向测试法测量单晶取向偏离度.结果表明,熔体超温处理对单晶取向偏离度和合金枝间溶质元素总含量的影响很小;随熔体超温处理温度由起始凝固温度1500℃升高至1640和1780℃,二次枝晶间距减小,细化率达14%-31%.
参考文献
| [1] | Gui Z L.Aviat Product Eng,1995; (4):12 (桂忠楼.航空制造工程,1995; (4):12) |
| [2] | Kolotukhin E V,Banm B A,Kuleshova E A,Larioiov V N,Tretyakova E E,Tyagunov G V.Steel,1992; (7):21 (Колотухинэв,БаумБА,кулешоваЕА,ЛарионовВН,ТретъяковаЕЕ,ТягуновГВ.СТАЛБ,1992; (7):21) |
| [3] | Wang Z,Li J G,Zhao N R,Jin T,Zhang J H.Acta Metall Sin,2002; 38:920 (王震,李金国,赵乃仁,金涛,张静华.金属学报,2002;38:920) |
| [4] | Chen G,Yu J W,Xie F Q,Fu H Z.Non-equilibrium Solidification of New Type Metallic Material.Beijing:Science Press,2004:205 (陈光,俞建威,谢发勤,傅恒志.非平衡凝固新型金属材料.北京:科学出版社.2004:205) |
| [5] | Zou M M,Zhang Jun,Liu L,Fu H Z.Acta Metall Sin,2008; 44:59 (邹敏明,张军,刘林,傅恒志.金属学报,2008;44:59) |
| [6] | Guo Z Q,Fu T,Wang N,Fu H Z.J Inorganic Mater,2002; 17:460 (郭振琪,付涛,王宁,傅恒志.无机材料学报,2002;17:460) |
| [7] | Kattamis T Z,Flemings M C.TMS AIME,1965; 233:992 |
| [8] | Liu L,Zhen B L,Banerji A,ReifW,Sommer F.Scr Metall Mater,1994; 30:593 |
| [9] | Yin F S,Sun X F,Li J G,Guan H R,Hu Z Q.Scr Mater,2003; 48:425 |
| [10] | Chen G L,Lu F Y.Acta Metall Sin,1997; 33:455 (陈长乐,陆富一.金属学报,1997;33:455) |
| [11] | Chen G,Yu J W,Xie F Q,Fu H Z.Acta Metall Sin,2001;37:488 (陈光,俞建威,谢发勤,傅恒志.金属学报,2001;37:488) |
| [12] | Yin F S,Sun X F,Guan H R,Hu Z Q.J Alloy Compd,2004; 364:225 |
| [13] | Huo Y P,Zheng J R.Non-equilibrium State Statistic Theory.Beijing:Science Press,1987:371 (霍裕平,郑久仁.非平衡态统计理论.北京;科学出版社,1987:371) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%