以激光熔覆法在低硅钢表面制备出高硅含量的Re-Si涂层.用扫描电镜、透射电镜、Mossbauer谱、X射线衍射等方法研究了硅钢基体和熔覆涂层的微观组织和室温超精细结构及其变化.结果表明,涂层与基体结合良好,自结合界面起至熔覆涂层表面的显微组织依次为平面晶、柱状树枝晶和细小树枝晶组织;熔覆涂层中存在6种可区别的Fe原子组态;涂层中含Si主要相为α-Fe类型相,以无序固溶体形式存在,其相对含量占69.6%(体积分数);α-Fe类型相中随Fe原子近邻Si原子数的增加,同质异能移位值增大,超精细磁场值减小.
参考文献
[1] | Hajji H,Okada K,Hiratani T,Abe M,Ninomiya M.J Magn Magn Mater,1996; 160:109 |
[2] | Ushigami Y,Mizokami M,Fujikura M,Kubota T,Fujii H,Murakami K.J Magn Magn Mater,2003; 254-255:307 |
[3] | Dong D Y,Liu C S,Zhang B,Miao J.Chin J Mater Rea,2007; 21:364 (董丹阳,刘常升,张滨,苗隽.材料研究学报,2007;21:364) |
[4] | Dong D Y,Liu C S,Zhang B,Miao J.J Univ Sci Technol Beijing,2007; 14:321 |
[5] | Pelletier J M,Renaud L,Fouquet F.Mater Sci Eng,1991;A134:1283 |
[6] | Yang S,Su Y P,Liu W J,Huang W D,Zhou Y H.Acta Phys Sin,2003; 52:81 (杨森,苏云鹏,刘文今,黄卫东,周尧和.物理学报,2003;52:81) |
[7] | Su Y P,Lin X,Wang M,Xue L,Huang W D.Chin Phys,2006; 15:1631 |
[8] | Song J L,Deng Q L,Hu D J,Chen C Y.Chin J Lasers,2005; 32:1441 (宋建丽,邓琦林,胡德金,陈畅源.中国激光,2005;32:1441) |
[9] | Zhao Y,Sheng Q,Wang C B,Zhang L M.Powder Metall Technol,2006; 24:407 (赵嫒,沈强,王传彬,张联盟.粉末冶金技术,2006;24:407) |
[10] | Li T,Li Y Z,Zhang Y H.J Phys Condens Matter,1907;9:1381 |
[11] | Li X N,Nie D,Dong C,Ma T C,Jin X,Zhang Z.Acta Phys Sin,2002; 51:115 (李晓娜,聂冬,董闯,马腾才,金星,张泽.物理学报,2002;51:115) |
[12] | Yuan X G,Xn D M,Zhang W D,Li Q C.Acta Metall Sin,1996; 32:1034 (袁晓光,徐达鸣,张卫方,李庆春.金属学报,1996;32:1034) |
[13] | Chen S Y,Liu C S,Fu G Q,Zhang J L,Cai Q K.Chin J Laser,2003; 30:1049 (陈岁元,刘常升,付贵勤,张继良,才庆魁.中国激光,2003;30:1049) |
[14] | Stearns M B.Phys Rev,1963; 129:1136 |
[15] | Ma R.Z,Xu Y T.The Theory of Mossbauer Spectra.Beijing:Science Press,1996:438 (马如璋,徐英庭.穆斯堡尔谱学.北京:科学出版社,1996:438) |
[16] | Teng G Q,Chao Y S.Chin J Nonferrous Met,2000; 10:27 (滕功清,晁月盛.中国有色金属学报,2000;10:27) |
[17] | Bai K C,Jiang Z Y,He K Y,Cheng L Z,Zhi J.Acta Metall Sin,1994; 30:67 (白魁昌,江自应,何开元,程力智,智靖.金属学报,1994;30:67) |
[18] | Chao Y S,Zeng F W,Yang Y L,Dong L Q,Chen S Y.Acta Metall Sin,2000; 36:235 (晁月盛,曾繁武,杨玉玲,董立秋,陈岁元.金属学报,2000;36:235) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%