系统研究了铝基非晶态合金Al-Co-Y体系中富Al区的非晶形成能力.形成非晶结构最佳成分为AlssCosY7,条带临界厚度为230μm.此体系的玻璃形成能力对合金成分十分敏感.具有高的玻璃形成能力的合金未呈现出明显的玻璃转变特征.相对Trg和△Tx判据,"相选择"理论在寻找最佳合金成分和表征玻璃形成能力与成分的关系中更为有效.在非晶相的形成过程中,其主要竞争相为fcc-Al,Al3Y和Al9 Co2相.
参考文献
| [1] | Ohtera K,Inoue A,Terabayashi T,Nagahama H,Masumoto T.Mater Trans JIM,1992; 33:775 |
| [2] | Inoue A,Sobu S,Louzguine D V,Kimura H,Sasamori K.J Mater Res,2004; 19:1539 |
| [3] | Inoue A,Onoue K,Masumoto T.Mater Trans JIM,1994;35:808 |
| [4] | Higashi K,Mukai T,Tanimura S,Inoue A,Masumoto T,Kita K,Ohtera K,Nagahora J.Scr Metall Mater,1992;26:191 |
| [5] | Inoue A,Matsumoto N,Masumoto T.Mater Trans JIM,1990; 31:493 |
| [6] | Inoue A.Prog Mater Sci,1998; 43:365 |
| [7] | Greer A L.Nature,1993; 366:303 |
| [8] | He Y,Shifler G J,Poon S J.J Alloy Compd,1994; 207:340 |
| [9] | Yang H W,Dong P,Wang J Q,Li Y.Mater Sci Eng,2007; A449-451:273 |
| [10] | Villars P,Prince A,Okamoto H.Handbook of Ternary Alloy Phase Diagrams.Vol.3,2nd Printing,Materials Park,OH:ASM International,1997:3092 |
| [11] | Klug H P,Alexander L E.X-ray Diffraction Procedures for Polyerystalline and Amorphous Materials.New York:John Wiley & Sons,Inc.,1974:618 |
| [12] | Wilde G,Sieber H,Perepezko J H.Scr Mater,1999; 40:779 |
| [13] | Perepezko J H,Hebert R J,Wu R I,Wilde G.J Non-Cryst Solids,2003; 317:52 |
| [14] | Perepezko J H.Prog Mater Sci,2004; 49:263 |
| [15] | Wang D,Li Y,Sun B B,Sui M L,Lu K,Ma E.Appl Phys Lett,2004; 84:4029 |
| [16] | Ma D,Tan H,Wang D,Li Y,Ma E.Appl Phys Lett,2005;86:191906 |
| [17] | Wang D,Tan H,Li Y.Acta Mater,2005; 53:2969 |
| [18] | Tan H,Zhang Y,Ma D,Feng Y P,Li Y.Acta Mater,2003;51:4551 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%