采用射频溅射法制备了纳米铁磁金属-半导体基体Fe0.35(ZnSe)0.65颗粒膜,并研究了其结构和磁特性.根据颗粒膜低场磁化率x(T)温度关系和不同温度下的磁滞回线,证实了在一定的温度范围内,颗粒膜中的纳米铁颗粒表现出磁性弛豫效应.当截止温度TB=50 K时.颗粒膜的磁性由超顺磁性转变为铁磁性.在截止温度以上,其饱和磁化强度Ms(T)温度关系符合Bloch的自旋波T3/2定律,探讨分析了自旋波常数增大的原因.
参考文献
| [1] | Chen T Y,Huang S X,Chien C L,Stiles M D.Phys Rev Lett,2006; 96:207203 |
| [2] | Hattink B J,Carcia del Muro M,Konstantinovic Z,Batlle X,Labarta A.Phys Rev,2006; 73B:045418 |
| [3] | Borcia I D,Beauvillain P,Bartenlian B,Gogol P,Megy R.J Magn Magn Mater,2006; 301:258 |
| [4] | Nunes W C,Socolovsky L M,Denardin J C,Cebollada F,Knobel M.Phgs Rev,2005; 72B:212413 |
| [5] | Chi J H,Ge S H,Liu C M,Kunkel H P,Zhou X Z,Williams G.J Appl Phys,2003; 93:6188 |
| [6] | Xiao G,Liou S H,Levy A,Taylor J N,Chien C L.Phys Rev,1986; 34B:7573 |
| [7] | Xiao G,Chien C L.J Appl Phys,1987; 61:3308 |
| [8] | Chantrell R W,Wohlfarth E P.J Magn Magn Mater,1983; 40:1 |
| [9] | Dai D S,Qian K M.Ferromagnetism.Beijing:Science Press,1987:207(戴道生,钱昆明.铁磁学.北京:科学出版社,1987:207) |
| [10] | Neel L.Ann Phys (Paris),1936; 5:269 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%