研究了强磁场对NiAl-Cr(Mo)-0.2Hf共晶合金微观组织和力学性能的影响.结果表明:强磁场处理后合金共晶胞内的Cr(Mo)层片发生碎化,共晶胞间的Cr(Mo)相呈现粗化的趋势,且合金中Cr(Mo)的化学成分发生了很大变化.分析为强磁场促进了合金中相间和胞界处的原子扩散、迁移,从而导致了合金组织形貌及成分的变化.强磁场处理后合金的室温压缩应变可达34%,比普通热处理提高近1倍;断裂韧性也得到一定程度的提高.
参考文献
| [1] | Miracle D B.Acta Metall Mater,1993;41:649 |
| [2] | Noebe R D,Bowman R R.Int Mater Rev,1993;38:193 |
| [3] | Guo J T.Ordered Intermetallic Compound NiAl Alloy.Beijing;Science Press,2003:104 (郭建亭.有序金属间化合物NiAl.北京:科学出版社,2003:104) |
| [4] | Misra A,Gibala R.Intermetallics,2000;8:1025 |
| [5] | Cline H E,Walter J L.Metall Trans,1970;1:2907 |
| [6] | Cline H E,Walter J L,Lifshin E,Russell R R.Metall Trans,1971;2:189 |
| [7] | Chen X F,Johnson D R,Noebe R D,Olliver B F.J Mater Res,1995;10:1159 |
| [8] | Yang J M,Jeng S M,BainK,Amato R A.Acta Mater,1997;45:295 |
| [9] | Guo J T,Cui C Y,Qi Y H,Ye H Q.J Alloys Compd,2002;343:142 |
| [10] | Guo J T,Cui C Y,Chen Y X,Li D X,Ye H Q.Intermetallics,2001;9:287 |
| [11] | Qin Q D,Zhao Y G,Zhou W,Cong P J.Mater Sci Eng,2007;A447:186 |
| [12] | Steinbach S,Ratke L.Mater Sci Eng,2005;A413-414:200 |
| [13] | Cao Z Q,Jia F,Zhang X G,Hao H,Jin J Z.Mater Sci Eng,2002;A327:133 |
| [14] | Asai T,Hirata S,Takeyama M,Matsuo T.Mater Sci Eng,2002;A329-331:828 |
| [15] | Chen Y X,Cui C Y,He L L,Guo J T,Li D X.Acta Metall Sin,1999;35:897 (陈玉喜,崔传勇,贺连龙,郭建亭,李斗星.金属学报,1999;35:897) |
| [16] | Qalter J H,Cline H E.Metall Trans,1970;1:1221 |
| [17] | Wang Q,Li D G,Wang K,Wang Z Y,He J C.Scr Mater,2007;56:485 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%