研究了不同Gd含量对二元NiAl合金组织以及室温和1100 ℃压缩性能的影响.结果表明,稀土Gd在NiAl中的固溶度很小,在合金晶内及晶界大量析出一种脆硬的新相--富Gd相.由于Gd的固溶强化和适量富Gd相产生的第二相强化,使得含0.10Gd合金的室温压缩强度高于二元NiAl的,而晶界上析出较多的富Gd相又使得含0.25Gd和0.50Gd合金的室温压缩强度较低;Gd的净化基体作用使得NiAl-Gd合金的室温压缩塑性高于二元NiAl的室温压缩塑性.含Gd合金在1100℃压缩,亦未出现应变软化现象.
参考文献
| [1] | Guo J T,Huai K W,Gao Q,Ren W L,Li G S.Intermetallics,2006;15:727 |
| [2] | Li S,Zhao D Q,Pan M X,Wang W H.J Non-Cryst Solids,2005;351:2568 |
| [3] | Xu J W.J Alloy Compd,2007;448:331 |
| [4] | Xia K,Xu X,Song D.Acta Mater,2004;52:841 |
| [5] | Guo J T.Ordered Intermetallic Compound NiAl Alloy.Beijing:Science Press,2003:81 (郭建亭.有序金属间化合物镍铝合金.北京:科学出版社,2003:81) |
| [6] | Vasiliev A L,Aindow M,Blackburn M J,Watson T J.Intermetallics,2005;13:741 |
| [7] | Huai K W.PhD Dissertation,Institute of Metal Research,Chinese Academy of Sciences,Shenyang,2006 (淮凯文.中国科学院金属研究所博士学位论文,沈阳,2006) |
| [8] | Chen W X,Hines J R,Wang Y.Adv Eng Mater,2004;6:876 |
| [9] | George E P,Liu C T.J Mater Res,1990;5:754 |
| [10] | Noebe R D,Bowman R R,Nathal M V.Int Mater Rev,1993;38:193 |
| [11] | Darolia R,Lahrman D,Field R.Scr Metall Mater,1992;26:1007 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%