研究了利用红外辐照快速加热(热冲击)与时效处理对γ-TiAl基合金显微组织的影响.结果表明,热冲击可将片层团平均尺寸为300 μm、片层间距为1.3 μm的粗大铸态近全片层组织处理成为片层团界面平直、片层间距为140 nm的亚稳态组织.经过1260 ℃,6 h时效处理后,形成片层团平均尺寸为40 μm,锯齿状片层团界面的稳态全片层组织.
参考文献
| [1] | Chan K S,Kim Y W.Metall Trans,1992;23A:1663 |
| [2] | Keller M M,Jones P E,Porter W J,Eylin D.JOM,1997;49 (5):42 |
| [3] | Zhang W J,Evangelista E,Francesconi L.Scr Mater,1996;35:41 |
| [4] | Zhang J,Zhang Z H,Shi J D,Zou D X,Zhong Z Y.Acta Metall Sin,1998;34:919 (张继,张志宏,石建东,邹敦叙,仲增墉.金属学报,1998;34:919) |
| [5] | Xie K,Wang J N,Tang J C,Luo C,Zhang J H,He Y H,Huang B Y.Rare Met Mater Eng,1999;28:248 (谢鲲,王健农,唐建成,罗成,张俊红,贺跃辉,黄伯云.稀有金属材料与工程,1999;28:248) |
| [6] | Yang J,Wang J N,Xia Q F,Wang Y.Mater Lett,2000;46:193 |
| [7] | Wu X H,Hu D.Scr Mater,2005;52:731 |
| [8] | Zhu H L,Matsuda J,Maruyama K.Mater Sci Eng,2005;A397:58 |
| [9] | Peng C Q,He Y H,Huang B Y,Liaw P K.Trans Nonferrous Met Soc Chin,2004;14:459 |
| [10] | Tang J C,Huang B Y,He Y H,Xie K.Trans Nonferrous Met Soc Chin,2000;10:10 |
| [11] | Hellwiq A,Palm M,Inden G.IntermetaUics,1998;6:79 |
| [12] | Ramanujan R V.Int Mater Rev,2000;45:217. |
| [13] | Peng C Q,Huang B Y,He Y H.J Mater Eng,2002; (2):27 (彭超群,黄伯云,贺跃辉.材料工程,2002; (2):27) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%