利用电容测试法和光电流技术研究了X80管线钢在NaHCO3/Na2CO3缓冲溶液中所成钝化膜的半导体性能和光电流特性,分析了成膜电位、成膜时间、Cl-浓度,溶液pH值以及成膜温度等因素对膜光电流响应的影响.结果表明,X80管线钢钝化膜的Mott-Schottky直线部分的斜率和光电流均为正,表明钝化膜呈现n型半导体特性.随着成膜电位的增加、成膜时间延长、溶液pH值升高、成膜温度及溶液中Cl-浓度的减小,Mott-Schottky直线部分的斜率和光电流响应均呈增大趋势,表明钝化膜内施上密度减小.
参考文献
| [1] | Sato N,Cohen M.J Electrochem Soc,1964; 111:512 |
| [2] | Carmezim M J,Simoes A M,Montemor M F,Da Cunha Belo M.Corros Sci,2005; 47:581 |
| [3] | Da Cunha Belo M,Walls M,Hakiki N E,Corset J,Picqenard E,Sagon G,Noel D.Corros Sci,1998; 40:447 |
| [4] | Rata A D,Chezan A R,Presura C,Hibma T.Surf Sci,2003; 35:341 |
| [5] | Kim J S,Cho E A,Kwon H S.Electrochim Acta,2001; 47:415 |
| [6] | Knauth P,Massiani Y.J Electroanal Chem,1998; 42:229 |
| [7] | Horowitz G.J Electroanal Chem,1983; 159:421 |
| [8] | Bardwell J A,Macdougall B,Graham M J.J Electrochem Soc,1988; 135:413 |
| [9] | Li D G,Feng Y R,Bai Z Q,Zheng M S.Appl Surf Sci,2007; 253:8371 |
| [10] | Cerischer H.Corros Sci,1989; 29:257 |
| [11] | Stimming U.Electrochim Acta,1986; 31:415 |
| [12] | Zeng Y M,Luo J L.Eleetrochim Acta,2003; 48:3551 |
| [13] | Macdonald D D.J Electrochem Soc,1992; 139:3434 |
| [14] | Davies D H,Burstein G T.Corrosion,1983; 36:416 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%