基于大型有限元软件Abaqus及其用户子程序(Umat)功能,开发了焊接残余应力与蠕变损伤耦合计算程序,对高温用焊接接头残余应力作用下的蠕变损伤行为进行有限元模拟,并与无焊接残余应力状态下的蠕变损伤情况进行比较.研究结果表明,在炉管焊接状态下,焊接残余应力最大值集中在焊缝和热影响区处,并且轴向与环向残余应力较高.在高温环境下,焊接接头初始态焊接残余应力较高,虽然在短时间内应力松弛到较低的水平,但其蠕变损伤仍较大程度地受焊接残余应力的影响,蠕变损伤分布与焊接残余应力的分布基本一致.
参考文献
| [1] | Hertzman S,Sandstrom R,Wale J.High Temp Technol,1987; 5(1):33 |
| [2] | Lundin C D,Khan K K,Yang D,Zieke W.Weld Res Counc Bull,1990; 354:1 |
| [3] | Viswanathan R,Foulds J R.ASME Pressure Vessels Pip Div Publ PVP,1995; 303:187 |
| [4] | Hyde T H,Sun W,Williams J A.Int J Press Vessels Piping,2002; 79:799 |
| [5] | Hyde T H,Becket A A,Song Y,Sun W.Comput Mater Sci,2006; 35:35 |
| [6] | Hyde T H,Sun W,Becker A A,Williams J A.Int J Press Vessels Pip,2004; 81:1 |
| [7] | Hyde T H,Sun W.Int J Press Vessels Pip,2002; 79:331 |
| [8] | Gong J M,Tu S D,Ling X,Yu H M.J Mater Eng,2000; 11:9(巩建鸣,涂善东,凌祥,喻红梅.材料工程,2000;11:9) |
| [9] | Kachanov L M.USSUR Div Eng Sci,1958; 8:26. |
| [10] | Zhang G D,Zhou C Y.Trans China Weld Inst,2007; 28(8):99(张国栋,周昌玉.焊接学报,2007;28(8):99) |
| [11] | Qian Z M.Master Dissertation,Nanjing University of Technology,2005(钱珍梅.南京工业大学硕士学位论文,2005) |
| [12] | Zhang G D,Zhou C Y.Trans China Weld Inst,2006; 27(12):85(张国栋,周昌玉.焊接学报,2006;27(12):85) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%