通过动电位极化曲线和电化学阻抗谱(EIS)的测试,研究了高矿化度溶液中矿化度对J55钢CO2腐蚀电化学行为的影响.结果表明:在高矿化度介质中,J55钢的CO2腐蚀为阴极控制.随溶液矿化度增大,腐蚀电位正移,腐蚀速率先升高,后降低,当矿化度为62.423 g/L时,腐蚀速率最大.随溶液矿化度增加,J55钢的CO2腐蚀由电化学步骤控制转变为传质和电化学步骤混合控制,并且矿化度越高,传质控制越明显.J55钢的电化学阻抗谱呈现3个时间常数,即高频容抗弧、低频感抗弧和低频容抗弧.随溶液矿化度增大,电荷传递电阻先减小后增大,在62.423 g/L左右出现极小值.
参考文献
| [1] | Kermani M B,Morshed A.Corrosion,2003; 59:659 |
| [2] | Lu M X,Bai Z Q,Zhao X W,Zhao G X,Luo J H,Chen C F.Corros Prot,2002; 23:105(路民旭,白真权,赵新伟,赵国仙,罗金恒,陈长风.腐蚀与防护,2002;23:105) |
| [3] | Schmitt G,Horstemeier M.In:Corrosion 2006,Houston:NACE,2006:06112 |
| [4] | Chen C F,Lu M X,Zhao G X,Bai Z Q,Yan M L,Yang Y Q.Acta Metall Sin,2003; 39:848(陈长风,路民旭,赵国仙,白真权,严密林,杨延清.金属学报,2003;39:848) |
| [5] | Videm K.In:Corrosion 2000.Houston:NACE,2000:00039 |
| [6] | Guo X P,Tomoe Y.Corrosion,1998; 54:931 |
| [7] | Zhang X Y,Yu G,Wang F P,Du Y L.Chem J Chin Univ,1999;20:1115(张学元,余刚,王凤平,杜元龙.高等学校化学学报,1999;20:1115) |
| [8] | Schmitt G.In:Hausler R H,Giddard H P eds.,Advances in CO2 Corrosion,Vol.1,Houston:NACE,1984:10 |
| [9] | Zhang X Y,Ke K,Du Y L.J Chin Soc Corros Prot,2000; 20:317(张学元,柯克,杜元龙.中国腐蚀与防护学报,2000;20:317) |
| [10] | Ikeda A,Mukai S,Ueda M.In:Corrosion 84,Houston:NACE,1984:289 |
| [11] | Zhang X Y,Wang F P,Du Y L.Acta Metall Sin,1999; 35:513(张学元,王凤平,杜元龙.金属学报,1999;35:513) |
| [12] | Garsany Y,Pletcher D,Sidorin D,Hedges W M.Corrosion,2004; 60:1155 |
| [13] | Nesic S,Postlethwaite J,Olsen S.Corrosion,1996; 52:280 |
| [14] | de Waard C,Milliams D E.Corrosion,1975; 31:177 |
| [15] | Chen C F,Lu M X,Zhao G X,Bai Z Q,Yah M L,Yang Y Q.Acta Metall Sin,2003; 39:94(陈长风,路民旭,赵国仙,白真权,严密林,杨延清.金属学报,2003;39:94) |
| [16] | Fu X T,Wang Z P,Lu S F,Zhu X H.Acta Pet Sin,2000; 21(3):89(付晓泰,王振平,卢双舫,祝孝华.石油学报,2000;21(3):89) |
| [17] | Bockris J O M,Drazic D,Despic A R.Electrochim Acta,1961; 4:325 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%