应用分子动力学研究了一个熔融Cu55团簇冷却过程中变为二十面体的结构变化.根据原子密度分布函数和对分布函数随温度变化的分析表明,在降温过程中由于原子之间连续地交换位置,团簇结构发生了三个阶段的变化:首先形成三壳层结构,继之初步形成四壳层结构,并在团簇内部开始形成由13个原子组成的二十面体结构,最终形成原子分布于4个壳层内具有二十面体结构的CU55团簇.模拟中由原子密度分布函数确定了不同壳层的原子位置.
参考文献
| [1] | Ercolessi F,Andreoni W,Tosatti E.Phys Rev Lett,1991;66:911 |
| [2] | Li T X,Ji Y L,Yu S W,Wang G H.Solid State Commun,2000;116:547 |
| [3] | Zhang Z,Hu W Y,Xiao S F.Phys Rev,2006;73B:125443 |
| [4] | Liu H B,Ascencio J A,Alvarez M P,Yacaman M J.Surf Sci,2001;491:88 |
| [5] | Xu S N,Zhang L,Zhang C B,Qi Y.Acta Metall Sin,2007;43:379(徐送宁,张林,张彩碚,祁阳.金属学报,2007;43:379) |
| [6] | Lee Y J,Maeng J Y,Lee E K,Kim B,Kim S,Han K K.J Comput Chem,2000;21:380 |
| [7] | Chushak Y G,Bartell L S.J Phys Chem,2001;105B:11605 |
| [8] | Valkealahti S,Manninen M.Phys Rev,1992;45B:9459 |
| [9] | Zhang L,Zhang C B,Qi Y.Chin Phys,2007;16:77 |
| [10] | Yang Q W,Zhu R Z,Wen Y H.Acta Phys Sin,2005;54:89(杨全文,朱如曾,文玉华.物理学报,2005;54:89) |
| [11] | Zhang L,Zhang C B,Qi Y.Phys Lett,2008;372A:2874 |
| [12] | Yildirim E K,Guvenq Z B.Modell Simul Mater Sci Eng,2006;14:947 |
| [13] | Nam H S,Hwang N M,Yu B D,Yoon J K.Phys Rev Lett,2002;89:275502 |
| [14] | Ikeshoji T,Koga K.Phys Rev,2001;63E:031101 |
| [15] | Yang Q W,Zhu R Z.Acta Phys Sin,2005;54:4245(杨全文,朱如曾.物理学报,2005;54:4245) |
| [16] | Qi W H,Wang M P,Li Z,Xie D.Chin J Nonferrous Metals,2005;15:1854(齐卫宏,汪明朴,李周,谢丹.中国有色金属学报,2005;15:1854) |
| [17] | Rosu M F,Pleiter F,Niesen L.Phys Rev,2001;63B:165425 |
| [18] | Haberland H,Issendorff B V.Phys Rev Lett,1996;76:1445 |
| [19] | Flelicke A,Kirilyuk A,Ratsch C,Behler J,Scheffler M,Von Helden G,Ferrando G.Phys Rev,Lett,2004;93:023401 |
| [20] | Chen S,Sommers J M.J Phys Chem,2001;105B:816 |
| [21] | Baumberger F,Greber T,Osterwalder J.Phys Rev,2000;62B:15431 |
| [22] | Martin D S,Maunder A,Weightman P.Phys Rev,2001;63B:155403 |
| [23] | Boisvert G,Lewis L J.Phys Rev,1997;56B:7643 |
| [24] | Trushin O S,Salo P,Ala-Nissila T.Phys Rev,2000;62B:1611 |
| [25] | Sprague J A,Montalenti F,Uberuaga B P,Kress J D,Voter A F.Phys Rev,2002;66B:205415 |
| [26] | Jacob T,Anton J,Sarpe-Tudoran C,Sepp W D,Fricke B,Bastug T.Surf Sci,2003;536:45 |
| [27] | Frantz J,Rusanen M,Nordlund K,KoponenIT.J Phys:Condens Matter,2004;16:2995 |
| [28] | Darby S,Mortimer-Jones T V,Johnston R L,Roberts C.J Chem Phys,2002;116:1536 |
| [29] | Mei J,Davenport J W,Fernado G W.Phys Rev,1991;43B:4653 |
| [30] | Liu J,Zhao J Z,Hu Z Q.Acta Metall Sin,2005;41:219(刘俊,赵九洲,胡壮麒.金属学报,2005;41:219) |
| [31] | Zhang L,Wang S Q,Ye H Q.Chin Phys,2006;15:610 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%