采用溶胶-凝胶法,以γ-环氧丙氧丙基三甲氧基硅烷(γ-GPTMS)和正硅酸乙酯(TEOS)为前驱体,在2A12铝合金表面制备了稀土铈盐(Ce(NO3)3)掺杂的有机-无机杂化膜,研究了铈盐掺杂浓度和涂层固化温度等工艺条件.通过极化曲线和电化学阻抗谱(EIS),比较了掺杂与未掺杂有机-无机硅烷杂化膜、铬酸盐转化膜和RE转化膜在3.5%NaCl(质量分数)溶液中的耐腐蚀性能.测试结果均表明,铈盐掺杂硅烷杂化膜的极化电阻比掺杂前增大了约13倍,并显著高于铬酸盐转化膜和RE转化膜.
参考文献
[1] | Yu X W,Cao C N,Yao Z M,Zhou D R,Yin Z D.Mater Sci Eng,2000; A284:56 |
[2] | Montemor M F,Simoes A M,Ferreira M G S.Prog Org Coat,2001; 43:274 |
[3] | Rivera B F,Johnson B Y,O' Keefe M J,Fahrenholtz W G.Surf Coat Technol,2004; 176:349 |
[4] | Zhu L P,Lu C,Xiong R Z.Ordnance Mater Sci Eng,2007;30(5):601(朱利萍,鲁闯,熊仁章.兵器材料科学与工程,2007;30(5):601 |
[5] | Guo C,Shi T,Zuo Y,Zhao J M,Xiong J P.ElectroplatFinish,2006; 25(9):44(郭超,石铁,左禹,赵景茂,熊金.电镀与涂饰,2006;25(9):44) |
[6] | Wang C,Jiang F.Electroplat Pollut Control,2001; 21(5):16(王成,江峰.电镀与环保,2001;21(5):16) |
[7] | Wang C,Jiang F,Lin H C.Rare Met Mater Eng,2003;32:130(王成,江峰,林海潮.稀有金属材料与工程,2003;32:130) |
[8] | Tang J L,Tang Y M,Zuo Y.Mater Prot,2006; 39(11):27(唐望磊,唐聿明,左禹.材料保护,2006;39(11):27) |
[9] | Subramanian V,van Ooij W J.Surf Eng,1999; 15:168 |
[10] | Tang N,van Ooij W J,Gorecki G.Prog Org Coat,1997; 30:255 |
[11] | Sundararajan G P,van Ooij W J.Surf Eng,2000; 16:315 |
[12] | Zhu D Q,van Ooij W J.Prog Org Coat,2004; 49:42 |
[13] | Zhu D Q,van Ooij W J.Electrochim Acta,2004; 49:1113 |
[14] | van Ooij W J,Zhu D Q,Prasad G,Jayaseelan S,Pu Y,Teredesai N.Surf Eng,2000; 16:386 |
[15] | Chou T P,Chandrasekaran C,Limmer S J,Seraji S,Wu Y,Forbess M J,Nguyen C,Cao G Z.J Non-Cryst Solids,2001; 290:153 |
[16] | Metroke T L,Gandhi J S,Apblett A.Prog Org Coat,2004; 50:231 |
[17] | Metroke T L,Kachurina O,Knobbe E T.Prog Org Coat,2002; 44:185 |
[18] | Metroke T L,Apblett A.Prog Org Coat,2004; 51:36 |
[19] | Wang Y H,Zhao J M,Zuo Y.Corros Prot,2005; 26:432(王禹慧,赵景茂,左禹.腐蚀与防护,2005;26:432) |
[20] | Cao J Y.The Technology and Application of Un-coated Surfaces Pretreatment.Beijing:Chemical Industry Press,2004:242(曹京宜.涂装表面预处理技术与应用.北京:化学工业出版社,2004:242) |
[21] | Hu J M,Liu L,Zhang J T,Zhang J Q,Cao C N.Acta Metall Sin,2004; 40:1189(胡吉明,刘惊,张金涛,张鉴清,曹楚南,金属学报,2004;40:1189) |
[22] | Leggat R B,Taylor S A,Taylor S R.Colloids Surf,2002; 210A:83 |
[23] | Montemor M F,Rosqvist A,Fagerholm H,Ferreira M G S.Prog Org Coat,2004; 51:188 |
[24] | Li Y S,Wright P B,Puritt R,Tran T.Spectrochim Acta,2004; 60A:2759 |
[25] | Song X L,Jiang N,Qu P,He X,Yang H P,Qiu G Z.Chi J Nonferrous Met,2006; 16:2126(宋晓岚,江楠,曲鹏,何希,杨海平,邱冠周.中国有色金属学报,2006;16:2126) |
[26] | Hu Z.Inorg Chem Ind,2007; 39:21(胡震.无机盐工业,2007;39:21) |
[27] | Cao C N,Zhang J Q.An Introduction to Electrochemical Impedance Spectroscopy.Beijing:Science Press,2002:156(曹楚南,张鉴清.电化学阻抗谱导论.北京:科学出版社,2002:156) |
[28] | Trabelsi W,Triki E,Dhouibi L,Ferreira M G S,Zheludkevich M L,Montemor M F.Surf Coat Technol,2006; 200:4240 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%