采用激光加工在中碳钢基体表面制备了成形良好、稀释率低、组织细密的Mn-Cu合金涂层.对合金涂层进行了电解腐蚀处理,涂层中的Mn原子被电解液溶解,Cu原千经扩散、团聚,生长并形成了纳米多孔Cu涂层.涂层的孔洞尺十为30-50 nm,具有高比表面积.Mn-Cu合金涂层的初始成分对纳米多孔Cu涂层的微观形貌有较大的影响.
参考文献
| [1] | Biener J,Hodge A M,Hayes J R,Volkert C A,Zepeda Ruiz L A.Nano Lett,2006;6:2379 |
| [2] | Ding Y,Chen M W,Jonah E.J Am Chem Soc,2004;126:6876 |
| [3] | Kan Y D,Liu W J,Zhong M L,Ma M X.Heat Treat Met,2008;33(3):43(阚义德,刘文今,钟敏霖,马明星.金属热处理,2008;33(3):43) |
| [4] | Sun Y,Xia Y.Nano Lett,2003;3:1569 |
| [5] | Jonah E,Aziz M J,Karma A,Dimitrov N,Sieradzki K.Nature,2001;410:450 |
| [6] | Huang J F,Sun I W.Adv Funct Mater,2005;15:989 |
| [7] | Ding Y,Young J,Jonah E.Adv Mater,2004;16:1897 |
| [8] | Pugh D,Dursun A,Corcoran S.J Electrochem Soc,2005;152B:455 |
| [9] | Lu X,Bischoff E,Spolenak R,Balk T J.Scr Mater,2007;56:557 |
| [10] | [1O]Jia F L,Yu C F,Deng K J,Zhang L Z.J Phys Chem,2007;111C:8424 |
| [11] | Wu D H,Ren J L,Chen S C.Fundamentals of Modern Materials Processing.Beijing:Tsinghua University Press,1997:338(吴德海,任家烈,陈森灿.近代材料加工原理.北京.清华大学出版社,1997:338) |
| [12] | Zhang Y K,Zhou J Z,Ye Y X.Laser Processing Technology.Beijing:Chemical Industry Press,2004:193(张永康,周建忠,叶云霞.激光加工技术.北京:化学工业出版社,2004:193) |
| [13] | Zhong M L,Liu W J,Ning G Q,Yang L,Chen Y X.J Mater Process Technol,2004;147:167 |
| [14] | Zhong M L,Liu W J,Zhang H J.Wear,2006;260:1349 |
| [15] | Lu H B,Li Y,Wang F H.Scr Mater,2007;56:165 |
| [16] | Kan Y D,Liu W J,Zhong M L,Ma M X,Zhang W M,Zhang H J.In:Laser Institute of America,ed.,Proceedings of Pacific International Conference on Application of Lasers and Optics 2008,Orlando:Laser Institute of America,2008:905 |
| [17] | Dursun A,Pugh D V,Corcoran S G.J Electrochem Soc,2003;150B:355 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%