通过静态质量损失实验、X射线物相分析、扫描电镜形貌观察及微区成分分析等手段,研究了FGH95合金在650,700和750℃下的抗熔盐热腐蚀行为及热腐蚀动力学规律.研究结果表明:FGH95合金在650℃具有较好的抗热腐蚀性;在700和750℃下,FGH95抗热腐蚀能力下降,腐蚀严重.FGH95热腐蚀层主要由NiO,Ni3S2,Cr2O3组成,在700℃下腐蚀层出现NiCr2O4,在750℃下腐蚀层出现NaCl.
参考文献
| [1] | Kane W M,Krupp U,Jacobs T,McMahon C J.Mater Sci Eng,2005; A402:42 |
| [2] | Bedir F,Alniak M O.Mater Sci Eng,2006; A429:295 |
| [3] | He F,Wang W X,Yang W H.J Aero Mater,2000; 20(1):22(何峰,汪武祥,杨万宏.航空材料学报,2000;20(1):22) |
| [4] | Chen H M,Hu B F,Li H Y.Acta MetaU Sin,2003; 39:30(陈焕铭,胡本芙,李慧英.金属学报,2003;39:30) |
| [5] | Hu B F,Chen H M,Song D.Acta Metall Sin,2003; 39:470(胡本芙,陈焕铭,宋铎.金属学报,2003;39:470) |
| [6] | Liu F J,Zhang M C,Dong J X.J Univ Sci Technol Beijing,2007; 29:704(刘丰军,张麦仓,董建新.北京科技大学学报,2007;29:704) |
| [7] | Seal S,Kuiry S C,Leyda A.Oxid Met,2001; 56:583 |
| [8] | Khalid F A,Hussain N,Shahid K A.Mater Sci Eng,1999;A265:87 |
| [9] | Singh H,Puri D,Prakash S,Ghosh T K.Mater Corros,2007; 58:857 |
| [10] | Sidhu T S,Prakash S,Agrawal R D.Mater Sci Eng,2006;A430:64 |
| [11] | Mohanty B P,Shores D A.Corros Sci,2004; 46:2893 |
| [12] | Broum M W,Elraghy T.J Electrochem Soc,1997; 144:2508 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%