采用吸铸法制备了直径为2-5 mm的[(Fe1-xCox)71.2B24Y4.8]96Nb4(x=0,0.1,0.2,0.3和0.4)合金棒.XRD测试表明,用适量的Co替换Fe可有效提高原始合金(Fe71.2B24Y4.8)96Nb4的玻璃形成能力,拓宽非晶形成范围.热分析结果显示所有的非晶合金均具有高的玻璃转变温度(Fg≥2850 K)和宽广的过冷液态区(△Tx≥297 K).此外,Co的替换明显改善了原始非晶合金的软磁性能,其中成分为[(Fe0.9Co0.1)71.2B24Y4.8]96Nb4的非晶合金的饱和磁化强度Ms达到26.6 kA/m,矫顽力Hc仅为59 A/m.热磁实验表明,随着Co含量的增加,非晶合金的Curie温度不断升高,最大值达到577 K,与初始合金相比提高了100 K,显著改善了原体系的热磁性能.
参考文献
| [1] | Duwez P,Lin S C H.J Appl Phys,1967; 38:4096 |
| [2] | Inoue A,Shinohara Y,Gook J S.Mater Trans JIM,1995;36:1427 |
| [3] | Inoue A,Zhang T,Takeuchi A.Appl Phys Lett,1997; 71:464 |
| [4] | Inoue A,Zhang W.J Appl Phys,1999; 85:4491 |
| [5] | Inoue A,Shen B L.Mater Trans JIM,2002; 43:766 |
| [6] | Shen T D,Schwarza R B.Appl Phys Lett,1999; 75:49 |
| [7] | Lin C Y,Tien H Y,Chin T S.Appl Phys Lett,2005; 86:162501 |
| [8] | Hu Y,Pan M X,Liu L,Zhao Y H,Zhao D Q,Wang W H.Mater Lett,2003; 57:2698 |
| [9] | Kim D H,Park J M,Kim D H,Kim W T.J Mater Res,2007; 22:471 |
| [10] | Hart Z,Zhang J,Li Y.Intermetallics,2007; 15:1447 |
| [11] | Shen B L,Inoue A,Chang C T.Appl Phys Lett,2004; 85:4911 |
| [12] | Park J M,Park J S,Kim D H,Kim J H,Fleury E.J Mater Res,2006; 21:1019 |
| [13] | Li F S,Shen B L,MakinoA,Inoue A.Appl Phys Lett,2007; 91:234101 |
| [14] | Greet A L.Nature,1993; 366:303 |
| [15] | Slater J C.J Appl Phys,1937; 8:385 |
| [16] | Um C Y,McHenry M E.IEEE Trans Magn,2004; 40:2724 |
| [17] | Egami T.Rep Prog Phys,1984; 47:1601 |
| [18] | He S L,He K Y,Shen B G,Zhang H W,Zhang S Y,Guo H Q.J Appl Phys,1999; 86:6301 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%