结合压下率理论模型,考察了连铸方坯在不同拉速下压下率的变化规律.结果表明,方坯压下率在轻压下入口处最大,沿拉坯方向线性减少;与板坯相比,两者的压下率值在轻压下入口处均相差不大,方坯压下率值在轻压下出口处较板坯小;拉速每增加0.1 m/min,方坯平均压下率减少约为0.04 mm/m.方坯压下速率的取值范围不受拉速影响,最大值和最小值分别为0.13和0.04 mm/min.压下速率沿拉坯方向呈线性减少,拉速越大,压下速率减少越慢;方坯的平均压下速率也不随拉速变化,保持定值0.088 mm/min,较板坯的平均压下速率小.
参考文献
| [1] | Sivesson P,Hsllen G,Widell B.Ironmaking Steelmaking,1998; 25:239 |
| [2] | Raja V R,Pal N,Jayaswal N P.Steel Times Int,2005;29(4):41 |
| [3] | Scholes A.Ironmaking Steelmaking,2005; 32:101 |
| [4] | Flemings M C.ISIJ Int,2000; 40:833 |
| [5] | Yim C H,Park J K,You B D,Yang S M.ISIJ Int,1996;36(z.):231 |
| [6] | Morwald K,Thalammer M,Federspiel C,Gould L.Steel Times Int,2003; 12(1):17 |
| [7] | Morsut L.MPT Int,2003; 26(2):44 |
| [8] | Hodl H,Thalhammer M,Stiftinger M,Schulz O,Gould L.MPT Int,2003; 26(3):74 |
| [9] | Shigeaki O,Masayuki K,Mamoru Y,Tatsuo M.ISIJ Int,1991,31:1400 |
| [10] | Ralph N,Karl-Heinz S.Steel Res,2003; 74:700 |
| [11] | Yamanaka A,Okuda M.Ironmaking Steelmaking,1999;26:64 |
| [12] | Lin Q Y,Zhu M Y.Acta Metall Sin,2007; 43:847(林启勇,朱苗勇.金属学报,2007;43:847) |
| [13] | Lin Q Y,Zhu M Y.Acta Metall Sin,2007; 43:1301(林启勇,朱苗勇.金属学报,2007;43:1301) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%