对热轧态和动态应变时效预变形态的316L奥氏体不锈钢进行了550℃下不同加载水平的疲劳蠕变实验.与热轧态相比,在应力控制的疲劳蠕变循环过程中,动态应变时效表现为位移的突然阶跃现象;动态应变时效预变形处理能有效地减小材料的循环应变幅度,提高材料的强度,推迟材料中出现位移阶跃现象的循环周次,延长材料的疲劳蠕变寿命.
参考文献
[1] | Plumbridge W J.J Mater Proc Technol,1996; 56:502 |
[2] | Qian K W,Li X Q,Xiao L G.J Fuzhou Univ (Nat Sei),2001; 29:8 (钱匡武,李孝琦,萧林钢.福州大学学报(自然科学版),2001;29:8) |
[3] | Chen W Z,Qian K W.Acta Metall Sin,1989; 25:132 (陈文哲,钱匡武.金属学报,1989;25:132) |
[4] | Peng K P,Chen W Z,Qian K W.Acta MetaU Sin,1993; 29:283 (彭开萍,陈文哲,钱匡武.金属学报,1993;29:283) |
[5] | Jiang H F,Zhang Q C,Chen X D.Acta Mater,2007; 55:2219 |
[6] | Jiang H F,Zhang Q C,Jiang Z Y,Wu X P.Acta Metall Sin,2005; 41:727 (江慧丰,张青川,蒋震宇,伍小平.金属学报,2005;41:727) |
[7] | Jiang H F,Zhang Q C,Xu Y H,Wu X P.Acta Metall Sin,2006; 42:139 (江慧丰,张青川,徐毅豪,伍小平.金属学报,2006;42:139) |
[8] | Hong S G,Lee S B,Byun T S.Mater Sci Eng,2007; A457:139 |
[9] | Mannan S L.Bull Mater Sci,1993; 16:561 |
[10] | Hong S G,Lee S B.J Nucl Mater,2004; 328:232 |
[11] | Zhang L,Jiang H F,Jiang H.Pressure Vessel Technology,2008; 25(7):6 (张莉,江慧丰,姜恒.压力容器,2008;25(7):6) |
[12] | Miguel M C,Vespignani A,Zapperi S.Nature,2001; 410:667 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%