研究了高温度梯度定向凝固条件下冷却速率对DZ4125合金中γ'相形态、分布和尺寸的影响.结果发现,随着冷却速率的增大,合金的枝晶逐渐细化.当冷却速率达到36.4 K/s时,合金的凝固组织由粗枝晶变为超细枝晶.在此过程中,γ'相从立方形逐渐球形化,且枝晶干γ'相的球化速度比枝晶间的γ'相球化速度快.同时,枝晶干和枝晶间γ'相尺寸逐渐减小,枝晶干和枝晶间γ'相的均匀化程度增加.枝晶间γ'相比枝晶干γ'相的尺寸大,这种差别随冷却速率的增大而减小.造成γ'相在形貌和尺寸上变化的根本原因是冷却速率的变化引起γ固溶体中溶质的过饱和度ΔX,过饱和γ固溶体的过冷度ΔT,γ'相脱溶析出的临界形核功ΔG*和溶质在γ固溶体中扩散系数D的改变.
参考文献
| [1] | Bhambri A K,Kattamis T Z,Morral J E.Matall Trans,1975:6B:523 |
| [2] | Ricks R A,Porter A J,Ecob R C.Acta Metall,1982:31:43 |
| [3] | Du W,Wei P Y,Li J G,Fu H Z,Sun J H.Acta Metall Sin,1998:34:356(杜炜,魏朋义,李建国,傅恒志,孙家华.金属学报,1998;34:356) |
| [4] | Liu Z Y,Shi Z X,She L,Chen R Z,Wang L B,Gu L Y.Acta Aero Astron,1995:16:335(刘忠元,史正兴,佘力,陈荣章,王罗宝,顾林喻.航空学报,1995;16:335) |
| [5] | Zupani(c) F,Bom(c)ina T,Kri(z)man A,Markoli B,Spai(c) S.Scr Mater,2002:46:667 |
| [6] | Guo X P,Fu H Z,Sun J H.Metall Trans,1997:28A:997 |
| [7] | McLean M.Directional Solidified Materials for High Temperature Service.London:The Metals Society,1983:4 |
| [8] | Turnbull D J.Chem Phys,1981:18:950 |
| [9] | Xiao J M.Alloys Phase and Phases Transition.Beijing:Metallurgical Industry Press,1987:233(肖纪美.合金相与相变.北京:冶金工业出版社,1987:233) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%