利用计算机编程建立了A1-Zn-Mg-Cu合金(7175铝合金)中α-Al,η相及α-Al大角度晶界原子集团模型,采用递归法计算合金中Zn,Mg,Cu和H的环境敏感镶嵌能、原子间相互作用能、Fermi能级和态密度等电子结构参数,分析了合金的应力腐蚀机理.计算结果表明:Mg,Cu和H容易在晶界偏析.Mg对H具有吸引作用,促进H在晶界偏析,引起晶界氢脆;Zn增大晶界与晶内的电位差,降低合金抗腐蚀性;Cu能减小晶界与晶内Fermi能级差,降低晶界与晶内的电位差,具有减缓合金腐蚀的作用.计算结果还表明:η相的Fermi能级最高,腐蚀过程中作为阳极优先溶解.由于η相俘获H,当晶界析出断续η相时可减弱晶界H的偏析,提高抗腐蚀性;但晶界连续分布η相则形成腐蚀通道,加速腐蚀进程.
参考文献
| [1] | David A L,Ray M H.Light Met Age,1991;2(9):II |
| [2] | Wang H B,Huang J F,Yang B.Mater Rev,2003;17(9):1(王洪斌,黄进峰,杨滨.材料导报,2003;17(9):1) |
| [3] | Ferrer C P,Koul M G,Connolly B J,Moran A L.Corro-sion,2003;59:520 |
| [4] | Ramgopal T,Gouma P L,Frankel G S.Corrosion,2002;58:687 |
| [5] | Liu Y.J Beijing Union Univ(Nat Sci),2006;20(1):31(刘洋.北京联合大学学报(自然科学版),2006;20(1):31) |
| [6] | Lue H.PhD Thesis,University of Science and Technology Beijing,1998(吕宏.北京科技大学博士学位论文,1998) |
| [7] | Huang X Y,Li Y H,Xiao J M.J Chin Soc Corms Prot,1984;4(1):42(黄显亚,李永洪,肖纪美.中国腐蚀与防护学报,1984;4(1):42) |
| [8] | Najjar D,Magnin T,Waner T J.Mater Sci Eng,1997,A238:293 |
| [9] | Xiao S X,Wang C Y,Chen T L.The Application of the Discrete Variational Method in the Density Functional Theory to Chemistry and Materials Physics.Beijing:Sci-ence Press,1998:92(肖慎修,王崇愚,陈天朗.密度泛函理论的离散变分方法在化学和材料物理学中的应用.北京:科学出版社,1998:92) |
| [10] | Ashby M F.Philos Trans R Soc London,1987;393A:322 |
| [11] | [111 Zhou D W,Peng P,Liu J S.Sci China,2006;49E:129 |
| [12] | Peng P,Han S C,Zheng C X,Liu R S,Jin T,Hu Z Q.Rear Met Mater Eng,2005;34:854f彭平,韩绍昌,郑采星,刘让苏,金涛,胡壮麒.稀有金属材料与工程,2005;34:854) |
| [13] | Liu G L.Acta Phys Sin,2006,55:1983(刘贵立.物理学报,2006;55:1983) |
| [14] | Liu G L,Li R D.Acta Phys Sin,2006;55:776(刘贵立,李荣德.物理学报,2006;55:776) |
| [15] | Haydock R.Solid State Physics.Vol.35,New York:Aca-demic Press,1980:216 |
| [16] | Harrison W A.Electronic Structure and the Properties ofSolids.San Francisco:Freeman,1980:551 |
| [17] | Slater J C,Koster G F.Phys Rev,1954;94:1498 |
| [18] | Wang L G,Wang C Y.Mater Sci Eng,1997;A234-236:52 |
| [19] | Gruhl W.Aluminum,1978;54:323 |
| [20] | Fan X G,Jiang D M,Shan C Z.Light Alloys Process Technol,2006;34(2):31(樊喜刚,蒋大鸣,单长智.轻合金加工技术,2006;34(2):31) |
| [21] | Liu X Y,Xu W,Foiles S M,Adams J B.Appl Phys Left,1998;72:1578 |
| [22] | Liu X G,Wang X W,Wang J Y,Zhang H Y.J Phys:Condens Matter,2005;17:4301 |
| [23] | Hu Q M,Xu D S,Li D.Acta Metall Sin,2002;38(Suppl.1):562(胡青苗,徐东升,李东.金属学报,2002;38(增刊1):562) |
| [24] | Malis T,Chaturvedi M C.J Mater Sci,1982;17:1479 |
| [25] | Zeng Y,Yin Z M,Pan Q L.J Cent South Univ Technol,2002;33:592(曾渝,尹志民,潘青林.中南工业大学学报,2002;33:592) |
| [26] | Liu X G,Wang X W,Wang J Y,Zhang H Y.J Mater SCi Technol,2006;22:135 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%