利用Gleeble 1500 热模拟试验机进行单轴热压缩实验,研究了含Al和不含Al两种过共析钢马氏体温变形和等温回火过程中的组织超细球化演变及超细球化组织的力学性能.结果表明:与马氏体等温回火相比,马氏体温变形加快马氏体的分解动力学,在较短的时间内即获得超细化(α+θ)复相组织.温变形过程中的组织超细化演变主要经历渗碳体粒子的析出与粗化及铁索体基体的动态回复和动态再结晶;而在等温回火过程中,铁索体主要发生静态回复和晶粒长大,并没有再结晶现象发生.合金元素Al的加入在等温回火和温变形过程中均抑制马氏体的分解,阻碍渗碳体粒子的粗化和铁素体晶粒的长大,导致复相组织的细化.同时,AI的加入使马氏体温变形和等温回火后所得超细化(α+θ)复相组织在不降低总延伸率的前提下,强度得以明显提高.
参考文献
| [1] | Sherby O D.ISIJ Int,1999;39:637 |
| [2] | Sherby O D,Walser B,Young CM,Cady EM.Scr Metall,1975;9:569 |
| [3] | Walser B,Sherby O D.Metall Trans,1979;10A:1461 |
| [4] | Wadsworth J,Lin J H,Sherby O D.Met Technol,1981;8:190 |
| [5] | Sherby O D,Oyama T,Kum D W,Walser B,Wadsworth J.J Met,1985;37(6):50 |
| [6] | Carsi M,Vicente A F,Sherby O D,Penalba F,Ruano O A.Mater Sci Forum,2007:539-.543:4826 |
| [7] | Oyama T,Sherby O D,Wadsworth J,Walser B.Scr Met-all,1984;18:799 |
| [8] | Taleff E M,Bramfitt B L,Syn C K,Lesuer D R,Wadsworth J,Sherby O D.Mater Charact,2001;46:11 |
| [9] | Furuhara T,Mizoguchi T,Maki T.ISIJ Int,2005;45:392 |
| [10] | Fu W,Furuhaxa T,Maki T.ISIJ Int,2004;44:171 |
| [11] | Tagashira S,Sakai K,Furuhara T,Maid T.ISIJ Int,2000;40:1149 |
| [12] | Chen W,Li L F,Yang W Y,Sun Z Q.Chin J Mater Res,2008;22:374 -(陈伟,李龙飞,杨王玥,孙祖庆.材料研究学报,2008;22:374) |
| [13] | Chen W,,Li L F,Yang W Y,Sun Z Q.Acta Metall Sin,2008;44:1069(陈伟,李龙飞,杨王玥,孙祖庆.金属学报,2008;44:1069) |
| [14] | Syn C K,Lesuer D R,Sherby O D.Metall Mater Trans,1994;25A:1481 |
| [15] | Lesuer D R,Syn C K,Whittenberger J D,Sherby O D.Metall Mater Trans,1999;30A:1559 |
| [16] | Tsuzaki K,Sato E,Furimoto S,Furuhara T,Maki T.Scr Mater,1999;40:675 |
| [17] | Ueji R,Tsuji N,Minamino Y,Koizumi Y.Acta Mater,2002;50:4177 |
| [18] | Xu S L,Li L F,Yang W Y,Sun Z Q.J Univ Sci Technol Beijing,2007;29:901(徐仕龙,李龙飞,杨王玥,孙祖庆.北京科技大学学报,2007;29:901) |
| [19] | Zhou J F,Jing T F,Gao Y W,Wang W,Zhao X,Song X Y.J Iron Steel Res,2007;19:45(周继锋,荆天辅,高聿为,王威,赵新,宋新宇.钢铁研究学报,2007;19:45) |
| [20] | Sun Z Q,Yang W Y,Qi J J,Hu A M.Mater Sci Eng,2002;A334:201 |
| [21] | Furuhara T,Kobayashi K,Maki T.ISIJ Int,2004;44:1937 |
| [22] | Song R,Ponge D,Raabe D.Acta Mater,2005;52:1075 |
| [23] | Song R,Ponge D,Raabe D,Kaspar R.Acta Mater,2005;53:845 |
| [24] | Furuhara T,Sato E,Mizoguchi T,Furimoto S,Maki T.Mater Trans.2002;43:2455 |
| [25] | Harrigan M J,Sherby O D.Mater Sci Eng,1971;7:177 |
| [26] | Zhou RF,Yang W Y,Sun Z Q,He J P.J Univ Sci Technol Beijing,2004;26:512(周荣锋,杨王玥,孙祖庆,何建平.北京科技大学学报,2004;26:512) |
| [27] | Leslie W C,Rauch G C.Metall Trans,1978;9A:343 |
| [28] | Li L F,Yang W Y,Sun Z Q.Acta Metall Sin,2003;39:419(李龙飞,杨王玥,孙祖庆.金属学报,2003;39:419) |
| [29] | Frommeyer G,Jimenez J A.Metall Mater Trans,2005;36A:295 |
| [30] | Wang B Q,Song X Y,Peng H F.Mater Des,2007;28:562 |
| [31] | Zuidema B K,Subraxnaanyam,Leslie W C.Metall Trans,1987;18A:1629 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%