03 μm,与未施加PEMF条件下制备的样品相比,分别降低了26.95%和60.13%;以PEMF制备的CoC2O4·2H2O为前躯体,在Ar气氛下加热分解获得了fcc结构的金属Co粉.
参考文献
[1] | Roure S,Bouvard D,Doremus P,Pavier E.Powder Metall,1999; 42:164 |
[2] | Gillia O,Bouvard D.Mater Sci Eng,2000; A279:185 |
[3] | Mao L C,Shah Z Q,Yin S H,Liu B,Wu Fo J Alloys Compd,1999; 293-295:825 |
[4] | Liu Y,Zhu Y,Zhang Y,Qian Y,Zhang M,Yang L,Wang C.J Mater Chem,1997; 7:787 |
[5] | Zheng Z S,Qu X H,Li Y P.Rare Met Mater Eng,2004;33:393(郑洲顺,曲选辉,李云平.稀有金属材料与工程,2004;33:393) |
[6] | Li Q H,Xiao W S,Liu Z H.Chin Powder Sci Technol,2008; 18:209(李启厚,肖松文,刘志宏.中国粉体技术,2008;18:209) |
[7] | Liu S,Xu K,Wang M.Int J Refract Met Hard Mater,2006; 24:405 |
[8] | Tikkanen M H,Taskinen A,Taskinen P.Powder Metall,1975; 18:259 |
[9] | Huang P Y.Powder Metallurgy Principle.Beijing:Metallurgical Industry Press,1982:50(黄培云.粉末冶金原理.北京:冶金工业出版社,1982:50) |
[10] | Niu H L,Chen Q W,Zhu H F,Lin Y S,Zhang X.J Mater Chem,2003; 13:1803 |
[11] | Wang F,Gu H Z,Zhang Z C.Mater Res Bull,2003; 38:347 |
[12] | Wang J Z,Qi J G,Du H L,Zhang Z B.J Iron Steel Res Int,2007; 14(4):75 |
[13] | Liu Z H.PhD Thesis,Central South University,Changsha,2007(刘志宏.中南大学博士学位论文,长沙,2007) |
[14] | Randall M German.Powder Metallurgy Science.Princeton:Metal Powder Industry,1994:168 |
[15] | Liu Y H,Liu P A.Principle and Application of X-Ray Diffraction Analysis.Beijing:Chemical Industry Press,2003:212(刘粤惠,刘平安.X射线衍射分析原理与应用.北京:化学工业出版社,2003:212) |
[16] | Inorganic Chemistry Teaching and Research Section of Tianjin University.Inorganic Chemistry.Beijing:China Higher Education Press,2002:146(天津大学兄机化学教研室.无机化学.北京:高等教育出版社,2002:146) |
[17] | Yao S T,Vekilov P G.Nature,2000; 406:494 |
[18] | Shi E W,Chen Z Z,Yuan R L,Zheng Y Q.Hydrothermal Crystallography.Beijing:Science Press,2004:80(施尔畏,陈之战,元如林,郑燕青.水热结晶学.北京:科学出版社,2004:80) |
[19] | Xu Y.Electromagnetics(Second Edition).Beijing:Science Press,2004:278(徐游.电磁学(第二版).北京:科学出版社,2004:278) |
[20] | Chen S.PhD Thesis,Central South University,Changsha,2003(陈松.中南人学博士学位论文,长沙,2003) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%