采用新型超快速变换HPVP-TIG电弧焊接工艺进行2219-T87高强铝合金焊接,研究脉冲电流特征参数对焊接接头组织和力学性能的影响.结果表明,加入超音频脉冲方波电流(UPSWC)作用后,铝合金焊缝区显微组织由粗大柱状晶转变为细小等轴晶,在焊缝区内除了等轴树枝晶外,还存在一种呈带状分布的极细小等轴非枝晶组织,同时焊缝熔合区宽度明显减小,焊接接头抗拉强度和断后伸长率显著提高.在一定范围内增加脉冲电流幅值,提高脉冲频率,减小占空比,可增强组织细化作用,提高接头力学性能.与未加入UPSWC作用相比,脉冲电流幅值100 A,脉冲频率40 kHz,占空比20%时,接头抗拉强度和断后伸长率分别提高约22%和111%.
参考文献
| [1] | Albertini G,Bruno G,Dunn B D,Fiori F,Reimers W,Wright J S.Mater Sci Eng,1997; A224:157 |
| [2] | Liu C F.Aeronaut Manufact Teehnol,2003; (2):22 (刘春飞.航空制造技术,2003;(2):22) |
| [3] | Yang C G,Guo X M,Hong Z F,Qian B N.Acta Metall Sin,2005; 41:1077(杨成刚,国旭明,洪张飞,钱百年.金属学报,2005;41:1077) |
| [4] | Qi B J,Cong B Q.Trans Chin Weld Inst,2008; 29:57 (齐铂金,从保强.焊接学报,2008;29:57) |
| [5] | Cong B Q,Qi B J,Zhou X G,Luo J.Trans Chin Weld Inst,2009; 30:25(从保强,齐铂金,周兴国,罗军.焊接学报,2009;30:25) |
| [6] | Cong B Q,Qi B J,Zhou X G,Luo J.Aerospace Mater Technol,2009; 39:71(从保强,齐铂金,周兴国,罗军.宇航材料工艺,2009;39:71) |
| [7] | Cook G E,Eassa E H.IEEE Trans Indust Applic,1985; 1A-21:1294 |
| [8] | Cong B Q.PhD Thesis,Beihang University,Beijing,2009 (从保强.北京航空航天大学博士学位论文,北京,2009) |
| [9] | Guo X M,Yang C G,Qian B N,Xu Q,Zhang H Y.Acta Metall Sin,2005; 41:397(国旭明,杨成刚,钱百年,徐强,张洪延.金属学报,2005;41:397) |
| [10] | Hunt J D.Mater Sei Eng,1984; A65:75 |
| [11] | Sun J S,Wu C S.Acta Phys Sin,2001; 50:209 (孙俊生,武传松.物理学报,2001;50:209) |
| [12] | Kou S,Le Y.Weld J,1986; 65:305 |
| [13] | Yunjia H,Frost R H,Olson D L,Edwards G R.Weld J.1989; 68:280 |
| [14] | Kou S,Le Y.Metall Trans,1988; 19A:1075 |
| [15] | Dvornak M J,Frost R H,Olson D L.Weld J,1991; 70:271 |
| [16] | Hao C Y,Yu E J,Ying H J,Shi C G.Acta Metall Sin,1996; 32:647(郝传勇,于尔靖,应慧筠,施成根.金属学报,1996;32:647) |
| [17] | Wang Q,He J C,Kawai S,Iwai K,Asai S.Acta Metall Sin,2002; 38:961(王强,赫冀成,川合悟,岩井一彦,浅井滋生.金属学报,2002;38:961) |
| [18] | Yu E J,Hao C Y,Ying H J,Shi C G,Li G H.Trans Chin Weld Inst,1996; 17:1(于尔靖,郝传勇,应慧筠,施成根,李敢红.焊接学报,1996;17:1) |
| [19] | Gutierrez A,Lippold J C.Weld J,1998; 77:123 |
| [20] | Reddy G M,Gokhale A A.J Mater Sci,1997; 32:4117 |
| [21] | Huang C,Kou S.Weld J,2000; 79:113 |
| [22] | Huang C,Kou S.Weld J,2001; 80:9 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%