以硝酸镁为起始原料, 胶棉液为添加剂, 在Si(100)衬底上成功地制备MgO薄膜, 结果表明, 胶棉液是形成MgO溶胶的关键组份; 薄膜的晶体结构与胶棉液的含量及退火温度有关. 同时, 用X射线衍射(XRD)、原子力显微镜(AFM)和透射电镜(TEM)对薄膜的微观结构进行了分析.
参考文献
[1] | Fork D K, Ponce F A, Tramontana J C, et al. Appl. Phys, Lett., 1991, 58: 2294-2296 |
[2] | Yoon J G. J. Korean. Phys. Soc., 1996, 29: ps648-651 |
[3] | DeSisto W J, Henry R L. J. Cryst. Growth., 1991, 109: 314-317 |
[4] | Seenzaki J, Mitsunaga O, Uchida T, et al. Jpn. J. Appl. Phys(1)., 1996, 38: 4195-4198 |
[5] | Fork D K, Anderson G B. Appl. Phys. Lett., 1993, 63: 1029-1031 |
[6] | Tarsa E J, Graef M D, Clarke D R, et al. J. Appl. Phys., 1993, 72: 3276-3283 |
[7] | Huang L S, Zheng L R, Blanton T N. Appl. Phys. Lett., 1992, 60: 3129-3131 |
[8] | Masuda A, Nshimoto K. J. Appl. Phys., 1994, 33: L 793-796 |
[9] | Kwak B S, Boyd E P, Zhang K, et al. Appl. Phys. Lett., 1995, 54: 2542-2544 |
[10] | Huang R, Kitai A H. Appl. Phys. Lett., 1992, 61: 1450-1452 |
[11] | Yoon J G, Kim K. Appl. Phys. Lett., 1995, 66: 2661-2663 |
[12] | Rywak A A, Burlitch J M, Loehr T M. Chem. Mater., 1995, 7: 2028-2038 |
[13] | Ho In-Chyuan, Xu Y H, Mackenzie J D. J. Sol-Gel. Sci. Technol., 1997, 9: 295-301 |
[14] | Kaneko Y, Mikoshiba, Yamashita T. Jpn. J. Appl. Phys., 1991, 30: 1091-1092 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%