采用化学气相浸渗法(CVI)，制备出三维Hi-Nicalon SiC/SiC陶瓷基编织体复合材料.经30h CVI致密化处理后，复合材料的密度达到2.5g.cm-3.所研制的三维SiC/SiC复合材料不仅具有较高的强度，而且表现出优异的韧性和类似金属材料非灾难性的断裂特征.复合材料的主要力学性能指标为：弯曲强度860MPa，断裂位移1.2mm，断裂韧性41.5MPa.m1/2，断裂功28.1kJ.m-2，冲击韧性36.0kJ.m-2.
Three dimensional textile SiC/SiC composites were fabricated by chemical vapor infil-tration,and their mechanical properties and microstructure were investigated.The density of the composites was 2.5g.cm-3 after the preform was infiltrated for 30 hours.The present composite materials exhibited excellent mechanical properties and metal-like failure behavior.The flexural strength and displacement were 860MPa and 1.2mm,respectively. Fracture toughness and work of fracture were 41.5MPa.m1/2 and 28.1kJ.m-2,respectively. The dynamic toughness was determined by using Charpy impact method and its value was 36.0kJ.m-2.
参考文献
| [1] | Evans A G.J.Am.Ceram.Soc.,1990,73: 187. |
| [2] | Naslain R.Key Eng.Mater.,1998,164-165: 3-8. |
| [3] | Golecki I.Mater.Sci.Eng.,1997,R 20: 37-124. |
| [4] | Lackey J,Hanigofsky J A,G B Freeman,et al.J.Am.Ceram.Soc.,1995,78: 1564-1570. |
| [5] | Stinton D P,Besmann T M,Lowden R A.Am.Ceram.Soc.Bull.,1988,67 (2): 36. |
| [6] | Inghels E,Lamon J.J.Mater.Sci.,1991,26: 5403. |
| [7] | Xu Y D,Zhang L T.J.Am.Ceram.Soc.,1997,80: 1897. |
| [8] | Xu Y D,Zhang L T,Cheng L F,et al.Carbon,1998,36: 1051. |
| [9] | Clegg W J,Kendall K,McN Alford N,et al.Nature,1990,347: 455-457. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%