为了探索利用EPR谱线对PTCR陶瓷的相变及PTC效应的机制研究的可能性,本文对掺Mn的BaTiO3基正温度系数热敏电阻(简称PTCR)陶瓷在120~450K温度范围内的电子顺磁共振谱进行了研究.得出了Mn2+离子EPR信号强度、9因子值和超精细耦合常数|A|值的温度分布,发现EPR参数与PTCR陶瓷相变有明显的对应关系,并给出微观结构上的初步解释.研究表明EPR谱线以及精细结构的分析可以为PTCR陶瓷的相变机制以及PTC效应的机制研究提供新的途径.
参考文献
[1] | Qiu Z W. The Electron Spin Resonance Spectra. Beijing: Academic Press, 1980.(in Chinese) |
[2] | Allak H M, Brinkman A W, Russell G J, et al. J. Appl. Phys., 1988, 63: 4530-4535. |
[3] | Eaton S S, Eaton G R. Bull. Mage. Res., 1979, 1: 130. |
[4] | Kutty T R N, Comathi L, Murugaraj P. Mat. Res. Bull., 1986, 21 (9): 1093-1102. |
[5] | Hari N S, Padmini P, Katty T R N. J. Mat. Sci., Mat. In Elect., 1997, 8: 15-22. |
[6] | Jida S S, Miki T. J. Appl. Phys., 1996, 80 (9): 5234-5239. |
[7] | Ikushima H. J. Phys. Soc. Jap., 1964, 19: 1986-1986. |
[8] | Mistsui T, Tatsugaki I, Nakamara E. An Introduction to The Physics of Ferroelectrics. Gordon and Breach, 1974. |
[9] | Matumura O. J. Phys. Soc. Jap, 1959, 14: 108-108. |
[10] | Anderson G H. Phys. Rev., 1960, 120: 1606. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%