研究了用固相法制备的高密度发光材料γ-Bi2WO6:Pr3+的结构、光致发光光谱、激发谱和γ-Bi2WO6的漫反射谱.由实验测得它的晶格参数为a=5.45A,b=16.42A,c=5.43A,密度Dx=9.53g/cm3.它的光致发光光谱主发射峰位于600、608、611、629nm,分别来自于pr3+的1D2→3H4、3P0→3H5、3P0→3H6、3P0→3F2跃迁的发射.其激发谱由位于约225~430nm范围内、最大值约在372nm的主激发带和450nm的激发峰组成;主激发带来自于基质,可能是基质的带间吸收、W-O间电荷迁移吸收和缺陷能级的吸收;450nm的激发峰来自于pr3+的3H4→3P2跃迁吸收.BWO:Pr3+的最佳掺杂浓度为0.8mol%左右.
参考文献
[1] | Bordun O M. J. Applied Spectroscopy, 1998, 65 (1): 149-151. |
[2] | Robertson J, Chen C W. Electronic structure and surface properties of SrBi2Ta2O9 and relatedoxides. In: Treece R E, et a1. ed Ferroelectric Thin Films VI. Symposium Warrendale, PA, USA.Mater. Res. Soc., 1998. 249-254. |
[3] | Blasse G, Dirken G J. Chem. Phys. Lett., 1982, 85 (2): 150-151. |
[4] | Blasse G, Dirken J. J. Solid State Chem., 1982, 42: 163-169. |
[5] | Gal'perin E L, Erman L Ya, Kolchin I K, et al. Russian J. Inorg. Chem., 1966, 11 (9): 1137-1142. |
[6] | Wolfe R W, Newnahm R E. Solid State Commun., 1969, 7 (24): 1797-1801. |
[7] | Rae A Avid, Thompson John G, Withers Ray L. Acta Cryst., 1991, B47: 870-881. |
[8] | JCPDS international center for Diffraction Data, Powder Diffraction File: Set 39, Inorganic andorganic, Philadelphia, USA: 1989, p97-98, No 39-265, 256a. |
[9] | Hodge L C. Mineral. Mag., 1970, 37: 705-707. |
[10] | Watanabe Akiteru. J. Solid State Chem., 1982, 41: 160-165. |
[11] | Knight Kevin S. Mineral. Mag., 1992, 56: 399-409. |
[12] | Seong Seeyearl, Yee Kyeong-Ae, Albright Thomas A. J. Am. Chem. Soc., 1993, 115 (5): 1981-1987. |
[13] | Pappalarto R. J. Lumin., 1976, 14: 159-193. |
[14] | Bode J H, Kuijt H R, Lahey M A J Th, et al. J. Solid State Chem., 1973, 8: 114-119. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%