使用常用的两步法,研究了基体掺杂不同物质对PMN陶瓷的烧结工艺和介电性能的影响.经研究发现,当掺杂lmo1%Li2O时,可以实现950~1000°C左右的中温烧结,材料的常温介电常数和介电损耗分别为13500和0.55%,都优于纯PMN.当掺杂2mol%时,可以将烧结温度降到800~900°C的低温烧结范围,且介电损耗明显下降.分析结果表明,材料的显微结构良好,材料的致密化程度较高.另外,掺加Li2O和SrO可以分别稍微减小和增加材料的弥散相变程度.同时本文还研究了PMN陶瓷的微观结构和介电弛豫的情况.
参考文献
[1] | Swartz S L, Shrout T R, Schulze W A, et al. J. Am. Ceram. Soc., 1984, 67: 311-315. |
[2] | Lejeune M, Boilot J P. J. Am. Ceram. Soc., 1985, 20: 493-499. |
[3] | Dong Heon Kang, Ki Hyun Yoon. Ferroelectrics, 1988, 87: 255-264. |
[4] | Lejeune M, Boilot J P. Am. Ceram. Soc. Bull., 1986, 64 (4): 679-682. |
[5] | Koichiro Tsuzuku, Masayuki Fujimoto. J. Am. Ceram. Soc., 1994, 77 (6): 1451-1456. |
[6] | Fr é d é ric Chaput, Jean-Pierre Boilot, et al. J. Am. Ceram. Soc., 1989, 72 (8): 1335-1357. |
[7] | Tomoaki Futakuchi, et al. Jpn. J. Appl. Phys., 1996, 35: 5113-5116. |
[8] | Swartz S L, Shrout T R. Mat. Res. Bull., 1982, 17: 1245-1250. |
[9] | Shrout T R, Halliyal A. Am. Ceram. Soc. Bull., 1987, 66: 704-711. |
[10] | Smolenskii G M. Proc. 2nd Int. Meet. Ferroelectr. (IMF-2), 1969(1970); 26-35. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%