用沸石合成法制备了CuCl14Pc/Y分子筛纳米复合材料(简称为CuCl14Pc/nano-Y),考察了合成条件对纳米复合材料的粒度影响.用XRD、ICP、TG-DTA、TEM、FTIR、UV-vis及催化反应等对其性能作了表征.结果表明:铜酞菁(CuCl14Pc)经过水热晶化后,部分被分装在纳米Y型分子筛的空腔中,其催化氧化性能较普通CuCl14Pc/Y分子筛复合材料有很大提高.
参考文献
[1] | Ichikawa M,Kimura T,Fukuoka A.Stud.Surf.Sci.Catal.,1994,84:335-342. |
[2] | De Vos D E,Jacobs P A.Catal.Today,2000,57:105-114. |
[3] | Ernst S,Traa Y,Deeg U.Stud.Surf.Sci.Catal.,1994,84:925-932 |
[4] | Thibault-Starzyk F,Paoton R F,Jacobs P A.Stud.Surf.Sci.Catal.,1994,84:1419-1424. |
[5] | Balkus K J,Khanmamedova A K,Dixon K M,et al.Appl.Catal.,A,1996,143:159-173. |
[6] | Balkus K J,Eissa M,Levado R.J.Am.Chem.Soc.,1995,117:10753-10754. |
[7] | Raja R,Ratnasamy P.Catal.Lett.,1997,48:1-10. |
[8] | Balkus K J,et al.Inorg.Chem.,1994,33:67-72. |
[9] | Vinod M P,Das T K,Chandwadkar A J,et al.Materials Chemistry and Physics,1999,58:37-43. |
[10] | Armengol E,Corma A,Fornes V,Appl.Catal.A,1999,181:305-312. |
[11] | Seelan S,Sinha A K,Srinivas D,et al.J.Mol.Catal.A,2000,157:163-171. |
[12] | Shevade S S,Raja R,Kotasthane A N.Appl.Catal.A,1999,18:243-249. |
[13] | Bedioui F,Roue L,Devynck J,et al.Stud.Surf.Sci.Catal.,1994,84:917-924. |
[14] | Castagnola N B,Dutta P K.J.Phys.Chem.B,1998,102:1096-1702. |
[15] | Yang H X,Li R F,Fan B B,et al.Stud.Surf.Sci.Catal.,2001,135:187-187. |
[16] | Fan B B,Li R F,Fan W B,et al.Journal of Nature Gas Chemistry,2000,9(2):157-163. |
[17] | Camblor M A,Corma A,Valencia S.Microporous and Mesoporous Materials,1998,25:59 74. |
[18] | Renzo F D.Catalysis Today,1998,41:37-40. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%