通过湿化学法合成了表面包覆硬脂酸的钛酸钡纳米复合微粒.通过FT-IR和XPS可以确认有机修饰层的极性基团通过化学键与无机内核结合;虽然BaTiO3结晶形态为无定型,但通过Raman和XRD依然可以确定四方相结构,TEM结果显示纳米微粒的尺寸在10~20nm左右.由于有机修饰层的存在影响了BaTiO3的成核机理和晶体生长过程中的择优取向.提出了硬脂酸表面有机修饰BaTiOa纳米微粒的形成机理,并给出其结构模型.
参考文献
[1] | Hagfeldt A,Gratzel M.Chem.Rev.,1995,95:49-68. |
[2] | Novak B M.Adv.Mater.,1993,5:422-433. |
[3] | Badley R D,Ford W T,McEnroe F J,et al.Langmuir,1990,6:792-801. |
[4] | Wu X,Wang D,Yang S.J.Colloid Interface Sci.,2000,222:37-40. |
[5] | Deacon G B,Philips R J.Coord.Chem.Rev.,1980,33:227-250. |
[6] | Godbole P D,Deshpande S B,Potdar H S,et al.Mater.Lett.,1991,12:97-101. |
[7] | Yamashita Y,Yoshida K,Kakihana M,et al.Chem.Mater.,1999,11:61-66. |
[8] | Begg B D,Finnie K S,Vance E R.J.Am.Ceram.Soc.,1996,79:2666-2672. |
[9] | Hagendorf C,Schindler K M,Doege T,et al.Surf.Sci.,1998,402-404:581-585. |
[10] | Mukhopadhyay S M,Chen TCS.J.Mater.Res.,1995,10:1502-1507. |
[11] | Asiaie R,Zhu W,Akbar S,et al.Chem.Mater.,1996,8:226-234. |
[12] | Lange F.Science,1996 (273):903-909. |
[13] | Kakihana M,Arima M,Nakamura Y,et al,Chem.Mater.,1999,11:438-450. |
[14] | 李强,高濂,严东生(LI Qiang,et al.),无机材料学报(Journal of Inorganic Materials),1999,14(1):150-154. |
[15] | 施尔畏,夏长泰,王步国(SHI Er-Wei,et al.),中国科学(E辑)(Science In China (Series E)),1997,27(2):126-133. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%